CA2154057C - Aqueous fast drying aerosol coating composition - Google Patents
Aqueous fast drying aerosol coating composition Download PDFInfo
- Publication number
- CA2154057C CA2154057C CA002154057A CA2154057A CA2154057C CA 2154057 C CA2154057 C CA 2154057C CA 002154057 A CA002154057 A CA 002154057A CA 2154057 A CA2154057 A CA 2154057A CA 2154057 C CA2154057 C CA 2154057C
- Authority
- CA
- Canada
- Prior art keywords
- water
- acrylic polymer
- weight
- composition
- solubilized
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
An aqueous aerosol coating composition, which includes a thermoplastic acrylic polymer solubilized in an aqueous solution of a monohydric alcohol.
The coating composition may further be blended with a controlling amount of a water soluble or water reducible acrylic polymer for imparting a desired degree of gloss and alkali resistance to a coating made from the aqueous aerosol coating composition. The compositions of this invention provide for improved drying rates, hardness and alkali resistance over current aqueous systems.
The coating composition may further be blended with a controlling amount of a water soluble or water reducible acrylic polymer for imparting a desired degree of gloss and alkali resistance to a coating made from the aqueous aerosol coating composition. The compositions of this invention provide for improved drying rates, hardness and alkali resistance over current aqueous systems.
Description
PATENT APPLICATION
OF
Hoinayoun Jamasbi FOR
AQUEOUS FAST DRYING AEROSOL COATING COMPOSITION
This invention generally relates to aqueous, also known as water-based, aerosol coating compositions and, more particularly, to a gloss-controlled aerosol coating composition having improved drying capability, hardness and alkali resistance over current water-based systenls.
Aerosol paint coinpositions that employ volatile organic solvents as a carrier and propellant for film-forming polymers are known and widely used.
However, the presence of organic solvents in aerosol compositions raise serious environmental concerns due to their toxic nature. Moreover, since such organic solvents are highly flammable, they create hazardous workplace conditions. While aqueous aerosol paint compositions have had some impact in resolving the problems of toxicity and flammability, a continuing concern is the longer drying times typically observed in water-based systems when coinpared to the faster drying times of organic solvent-based aerosol systems.
Furthermore, high gloss aerosol paint compositions, which are typically solvent based, are generally not suitable for coating solvent-sensitive surfaces, such as the surfaces of leather substrates. The present invention addresses this problem by providing for high gloss aerosol paint compositions that do not damage or mar such underlying solvent-sensitive substrate surfaces.
A variety of polymers sucli as acrylics, alkyds, epoxy esters, and vinyl polymers and copolymers may be used in aqueous aerosol compositions as film-forming polymers, which are also known as film formers. Water-based aerosol paint formulations having a mixture of dimethyl ether, water and a water-soluble solvent, such as monohydric alcohol, as a carrier and a propellant are known. The dimethyl ether-based propellant system is said to provide for water-soluble (WS) polymers and water-dilutable [also known as water-reducible (WR)] emulsion polymers that are useful as film-forming polymers.
U.S. Pat. No. 4,450,253 (the Suk patent) describes a film-forming polymer comprising an oil-modified acrylic ester polymer rendered water-soluble by neutralization witli a base, such as ammonia or an amine. This film-forming polymer is applied to a substrate by eniploying a single phase, water-based carrier and propellant system having dimethyl ether, water and water-soluble polar organic solvents. The Suk patent at column 6, lines 56 through 64 erroneously identified a Rohm and Haas Company product, Acrysol WS-24 1) 2 1 t5 4 0 ~J' 7 DN93-176 acrylic dispersion resin as an oil-nlodified acrylic acid ester suitable as a film-forming polymer. This is an erroneous identification of the chemical composition of Acrysol't WS-24 acrylic dispersiort resin, which is typically supplied at 36 % solids in water and is not oil-modified. Also, it is not oil-modified in any variation of the invention as described in the Suk patent.
Furthermore, there is no suggestion in the Suk patent that an acrylic dispersion resin, not modified by oil, can be employed as a film-forming polymer. However, a critical aspect of the invention in the Suk patent is to film-forming polymers that must be oil-rnodified ester polymers which are solubilized and dissolved in the liquid phase propellant-solvent solution provided by the dimethyl ether, water and at least one polar solvent, such as monohydric alcohol, (Specification, column 5, lines 32 through 37). Therefore, since Acrysol WS-24 acrylic dispersion resin is not oil-modified its identification as a drying oil-modified polymer was in error.
The present invention is directed to an aqueous aerosol coating composition comprising a thermoplastic acrylic polymer solubilized in an aqueous solution of a monohydric alcohol to form a solubilized acrylic solution, the thermoplastic acrylic polymer having a weight average molecular weight in the range of 105,000 to 200,000.
The aqueous aerosol coating composition further comprises a blend of the solubilized acrylic solution with a controlling amount of a water-based acrylic polymer for providing a desired degree of gloss and alkali resistance, the water-based acrylic polymer being selected from the group consisting of a water-soluble acrylic polymer, water-reducible acrylic polymer and a combination thereof.
The present invention is also directed to a rnethod of producing an aqueous coating composition comprising, adding a monohydric alcohol to water form an aqueous solution, solubilizing a thermoplastic acrylic polymer having a weight average molecular weight in the range of 105,000 to 200,000 in the aqueous solution to form a solubilized acrylic solution, blending a controlling amount of a water-based acrylic polymer with t11e solubilized acrylic solution to provide a desired degree of gloss and alakli resistance to a coating resulting from the aqueous coating composition.
While aqueous-based carrier and propellant systems have made some improvements over organic solvent-based systerns, furthei- improvements in drying time as measured by set-time, dry-to-touch time and tack-free time are required. The present invention addresses the problems of longer drying times typically observed in conventional aqueous aerosol systems, which utilize oil modified acrylics as film formers.
The present invention furtller provides for environmentally safe aqueous aerosol coating compositions which produce coatings having improved alkali resistance, hardness and gloss that equals or exceeds one normally seen in coatings employing solvent-based aerosol systems.
Generally, monohydric alcollols do not solubilize acrylic polymers, such as, poly(methyl methacrylate) [PMMA]. However, it llas been unexpectedly discovered that certain thermoplastic polymers and copolymers of esters of the methacrylic acid, solubilize in certain mixtures of alcohol and water.
Compared to other organic solvents, these solutions dry rapidly at room temperature, to produce hard and tough films. Thermoplastic acrylic polymers, as defined herein, are those 100 % solid thernloplastic acrylic polymers produced as powders or pellets. A wide variety of thernloplastic acrylic polymers including polymers as well as copolymers, described below, are suitable as film formers in the aerosol compositions of the present invention.
These thermoplastic acrylic polymers are provided with a weight average molecular weight in the range of 105,000 to 200,000, preferably in the range of 105,000 to 120,000 and most preferably 105,000. The weight average molecular weight, as defined herein, is the mean of the weight relative molecular weights of the weight fractions as describeci on pages 6-10, Chapter II of The Characterization of Polymers published by Rohm and Haas Company, Philadelphia, Pennsylvania in 1976. The weight average molecular weights are determined by gel permeation chromatography as described on page 4, Chapter IV of The Charncterization of Polymers published by Rohm and Haas Company, Philadelphia, Pennsylvania in 1976, utilizing polymetllyl methacrylate as the standard.
These thermoplastic acrylic polymers exhibit a glass transition temperature (Tg) varying from 35~ C to 105~ C, preferably from 35 C to 40 C
and most preferably 40* C. The Tg is defined as that temperature at which the properties of the polymer, sucli as, viscosity, impact resistance, hardness, undergo substantial changes. The 'Tg of the acrylic polymer is calculated by substituting the weight percentages and the Tgs of the monomeric components of the acrylic polymer in the well known Fox Equation described in Bulletin of American Physics Society, Vol. 1, Issue 3, page 123 (1956) and on pages 20-21, Chapter IV of The Characterization of Polymers published by Rohm and Haas Company, Philadelphia, Pennsylvania in 1976.
The thermoplastic acrylic polymers suitable for use in the aerosol composition df the present invention have an acid number in the range of 2 to 12, preferably in the range of 3 to 4. The acid number, as defined herein, is a 4 ~~~~~ ~7 DN93-176 number expressed as milligrams of potassium hyciroxide divided by grams of the neutralized polymer.
These thermoplastic acrylic polymers may be prepared by well known polymerization techniques, such as, suspension polymerization and emulsion polymerization of ethylenically unsaturated monomers. Suspension polymerization is preferred. The acrylic content results from the polymerization of acrylate or methacrylate esters, sucli as, for example, methyl acrylate, ethyl acrylate, butyl acrylate, methyl methacrylate, ethyl methacrylate, butyl methacrylate, i-butyl methacrylate, acrylic acid, ulethacrylic acid, and acryloxypropionic acid. The thermoplastic acrylic polymers are preferably prepared by suspension polynlerizing ethyl methacrylate and methacrylic acid or methyl methacrylate, etllyl acrylate and methacrylic acid, the former being the most preferred.
Among the commercially available thermoplastic acrylic polymers suitable for use herein are those made by Rohm and Haas Company, Philadelphia, Pennsylvania, under the trademark AcryloidU solid grade acrylic resins, which are available in 100% solid powder or pelletized form.
These thermoplastic acrylic polymers are solubilized, preferably at room temperature, in a previously prepared aqueous solution of monohydric alcohol, such as isopropanol, n-butanol or 3A alcohol (by weight-95% ethanol and 5%
isopropanol) to fornl a solubilized acrylic solution. Isopropanol is preferred.
The aqueous solution is produced by dissolving by weight 60% to 95%, preferably 70% monohydric alcohol in water. The term "solubilized" as defined herein means "dissolved" or "go in solution." It is desirable to dissolve monohydric alcohol in water before solubilizing the thermoplastic acrylic polymer therein. Such a step appears to prevent the alcohol from swelling the polymer and causing haze in the resulting aqueous solution.
Table 1 below provides the solubility data obtained by solubilizing 40% by weight of the thermoplastic acrylic polymer in various monohydric alcohols at various alcohol to water weight ratios:
Table 1 Alcohol/water N-butanol 3A alcohol (95%
ethanol, 5% IPA) 50/50 Insoluble Insoluble 60/40 Partially soluble Insoluble 70/30 Soluble Partially soluble 80/20 Soluble Partially soluble 90/10 Soluble Soluble 100% Alcohol Insoluble Insoluble S 15110 5 r DN93-176 The weight percentage of the thermoplastic acrylic polymer being solubilized in the aqueous solution of monohydric alcohol is adjusted in accordance with the desired drying rate of the resultant coating. By lowering the weight percentage of the solubilized thermoplastic acrylic polymer, faster drying rates of the resultant coating composition are achieved. The weight percentage of the thermoplastic acrylic polymer solubilized in the aqueous solution of monohydric alcohol and water may be varied from 5% to 45%, preferably from 30% to 40%, most preferably at 40%, all in the weight percentage of the solubilized acrylic solution.
Table 2 below provides the solubility range of the thermoplastic acrylic polymer (Resin) solubilized at various isopropanol (IPA) to water weight ratios:
Table 2 IPA/Water 30% solid Resin 40% solid Resin 50% solid Resin 50/50 Insoluble Insoluble Insoluble 60/40 Insoluble Insoluble Insoluble 70/30 Soluble Soluble Soluble 80/20 Soluble Soluble Soluble 90/10 Soluble Soluble Soluble 100% IPA Insoluble Insoluble Insoluble The appearance of the coating resulting from the foregoing aerosol coating composition is flat. However, the gloss of the resultant coating may be varied by blending the solubilized acrylic solution. with a controlling amount of a water-based acrylic polymer. The "controlling amount" is defined as the amount of water-based acrylic polymer in weight percentage sufficient to achieve a desired degree of gloss and alkali resistance to a coating resulting therefrom. By increasing the amount of the water-based polymer blended with the solubilized acrylic solution, one is able to achieve a more glossy coating.
The water-based acrylic polymers suitable for use in the present invention comprise a water-soluble acrylic polymer, a water-reducible acrylic polymer or a combination of the two. The water-soluble acrylic polymer is preferred.
The water-soluble acrylic polymer suitable for use in the present invention is provided with a weight average molecular weight in the range of 20,000 to 250,000, preferably 200,000, as determined by gel permeation chromatography, based on poly methyl methacrylate as the standard, an acid number typically in the range of 30 to 160, preferably 100 and a Tg in the range of 30 C to 140 C, preferably 45 'C. The water-soluble acrylic polymer comprises from about 40%
to 60% Butyl acrylate and 20% to 40% methyl nlethacrylate and with lower levels of styrene and methyl acrylate. The desired degree of gloss and alkali resistance on the coatings produced from the aerosol coating composition of the present 6 9w It 5 4 0 5) 7 DN93-176 invention is obtained by blending by weight 2% to 12%, preferably 8%, of the water-based acrylic polymer with the solubilized acrylic solution. These weight percentages are based on the total weight of the blend comprising the water-soluble acrylic polymer and the solubilized acrylic solution.
A number of water-soluble acrylic polymers sold by Rohm and Haas Company, under the trademark known as Acrysol@ acrylic dispersion resins are suitable for use in this invention.
As stated earlier, the water-based acrylic polyiner may comprise a water-reducible, low molecular weight acrylate copolymer having copolymerized units of an alkyl acrylate and an alkyl methacrylate, wherein the alkyl group has 3 to 5 carbon atoms. The preferred copolymers comprise 5% to 20 % butyl acrylate and from 30% to 60 % isobutyl methacrylate by weight. In addition, the composition may comprise 10% to 30 % by weight of a copolyn-ierized drying oil, such as, linseed oil, soya oil, tung oil, sunflower oil or other polyunsaturated oils.
Finally, the composition may comprise 10% to 20 % by weight of olefinically unsaturated acid, or acid anhydride, such as acrylic acid, methacrylic acid, maleic acid and the like or an anhydride thereof. The weight average molecular weight of the copolymer is in the range of 300 to 20,000, preferably from 6000 to 12,000 and most preferably from 8000 to 10,000. The desired. clegree of gloss and alkali resistance on the coatings produced from the aerosol coating composition of the present invention is obtained by blending by weight 2% to 30%, preferably 8%, of the water-reducible, low molecular weight acrylate copolymer with the solubilized acrylic solution. These weight percentages are based on the total weight of the blend comprising the water-reducible, low molecular weight acrylate copolymer and the solubilized acrylic solution.
A water-reducible, low molecular weight co-polymer of butyl acrylate and isobutyl methacrylate having a weight average molecular weight of 9000 is most preferred.
As stated earlier, the water-based acrylic polymer may comprise a combination of water-soluble and water-reducible acrylic polymers. In order to form such a combination, the water-reducible acrylic polymer is neutralized and the viscosity reduced with water to prevent precipitation of the polymer.
The neutralization can occur before or after the dryers are added to the polymer but typically before reduction with water. After water is adcled, the water-soluble acrylic polymer can be added to form the combination. If the above order of addition is not adliered to, it would be more difficult to form the combination of water-soluble and water-reducible acrylic polymers.
The weight ratio of the water-soluble acrylic polymer to the water-reducible, low molecular weight copolymer should be 20/80 to 80/20, while the 7 I o d~ DN93-176 preferred weight ratio should be from 40/60 to 60/40. When weight ratios are outside of the above ranges, the combinations are less stable and the coatings produced therefrom are inferior.
The present invention contemplates an aerosol composition adopted for providing a continuous film on a sulistrate upon discllarge frorn suitable containment means, such as, for example, an aerosol can. The propellant-active carrier system employed in the present invention preferably includes dimethyl ether and water. Dimethyl ether is a colorless, stable, polar liquid with a boiling point of minus 25 C. The aerosol composition of the present invention may comprise from 5 % to 60 %, preferably from 25 % to 50 % of dimethyl ether by weight, based on the total weight oE the aerosol composition.
While it is preferred that dimethyl ether is the sole propellant, under some circumstances, however, 0 % to up to 50 % by weight of dimethyl ether may be replaced by another liquid propellant, such as, an aliphatic llydrocarbon or a fluorinated hydrocarbon. Further, if desired, a gaseous propellant, such as nitrogen, carbon dioxide, nitrous oxide, may also be used.
Water is present in the composition of the present invention in an amount varying from 10 % to 70 %, preferably varying from 20 % to 60 % by weight of the total weight of the aerosol paint composition.
The aerosol coating composition of the present invention may further include, additives, such as a surfactant, pigment, pH stabilizer, antifoam agent, plasticizer, drying agents. In general, there will be less than 20 %, preferably less than 15 % by weight, based on the total weight of the composition, of the pigment. Suitably, the remaining foregoing additives, when present, would not exceed 3 % by weight, based on the total weight of the composition, for each additive, and usually only up to 1'I~, or 2% of each other adctitive would be present.
A blend of a thermoplastic acrylic polymer solubilized in a previously prepared aqueous solution of a monohydric alcollol with a water-based acrylic polymer in a water-based carrier and propellant system having dimethyl ether and water provides paiilt compositions with the desired film-forming and drying properties that are not obtained when the water-reducible, low molecular weight copolymer is einployed without the water-soluble acrylic polymer. Coating properties are further enhanced, when the water-reducible low molecular weight polymer undergoes air cure.
The present coating composition is suitable for use in many coating applications, such as, f'or example, wood finishes, printing inks, coatings on solvent sensitive substrates, such as, leather, sealers, over print varnishes, label varnishes, paper coatings, floor finishes, ceramic binders, vacuum metallized FW~ 5 4 0 5 7 coatings, coatings over polymeric substrates, traffic and zone marking paints, glaze coatings, wall coatings, clear coatings on delicate substrates, such as those of art objects.
The following test procedures were employed in evaluating the physical and chemical properties of the foregoing aerosol coating compositions. Unless and otherwise stated, all the tests were conducted under the standardized procedures developed by The American Society of Testing Materials, (ASTM), Philadelphia, Pennsylvania.
TEST PROCEDURES
- Dry to Touch time ......................ASTM D-1640 - Gloss ..............................................ASTM D-523 (The 20 degree and 60 degree gloss were measured with glass meters manufactured by the Gardner Instrument Company).
- Pencil Hardness ..........................ASTM D-1737 (6H being the hardest pencil and 6B being the softest pencil) - Cross Hatch Adhesion ...............ASTM D-3359 (on the scale of 1 through 10, 1 represents poor adhesion and 10 represents no loss of adhesion) - Water resistance ....................................A spot of water was left on the coated surface for a specified length of time. Pencil hardness was measured at the start and at the end of the test.
- Alkali resistance ...........................A spot of 7% solution of NH4OH
was left on the coated surface for a specified length of time. Appearance was checked at the start and at the end of the test.
- Water immersion .........................A coated panel was immersed in water for 2 hours. Pencil hardness was measured at the start and at the end of the test.
- Wet adhesion ................................Cross hatch adhesion was measured immediately after the coated panel was removed from the water immersion test described above. Another cross hatch adhesion was measured 2 hours later.
Some embodiments of the invention will now be described in detail in the following examples.
The three clear water-based compositions were prepared as follows:
85 parts by weight of isopropyl alcollol was dissolved in 15 parts by weight of deionized water to form an aqueous solution. Isopropyl alcohol @ 91%
strength with a flash point of 18 C , vapor pressure of 34 mm Hg at 20 C and a specific gravity of 0.818 at 20 C supplied by Union Carbide Inc., was used.
100%
9 21 ~4 0 5r 7 DN93-176 solid pellets of the thermoplastic acrylic polymer were then dissolved in the the aqueous solution at 40% by weight of the solution.
To the above described solution, water-reducible, low molecular weight copolymer at three different strengths, namely 27%, 19% and 0% by weight, was added to analyze the effect of the water-reducible, low molecular weight copolymer on gloss, adhesion, alkali resistance, and water spot effect on the coating resulting therefrom.
Table 3 below provides the composition of the three sample formulations.
Table 3 COMPONENTS Sample A Sample B Sample C
40% solution of the thermoplastic 12% 20% 39%
acrylic polymer in 85/15 IPA/Water water-reducible, low rnolecular 27% 19% 0%
weight acrylate copolymer 85/15IPA/Water 61% 61 h 61%
TOTAL 100% 100% 100%
Each of these sample formulations were tested for 60 degree gloss, cross hatcli adhesion, alkali resistance (2 hours), and water resistance (2 hours).
Adhesion of 10 demonstrates the best adhesion. It is clear from Table 4, below, that there is a direct relationship between the amount of the water-reducible, low molecular weight acrylate copolymer present in the formulation and the resulting gloss of the overall system, i.e., as the amount of the water-reducible, low molecular weight acrylate copolymer is increased, the gloss of the coating resulting therefrom is also improved.
Table 4 TESTS Sample A Sample B Sample C
60 degree gloss 90+/-2 70+/-2 50+/-2 Adhesion 10 10 10 Alkali resistance (2 hrs) fail fail pass Water resistance (2 hrs) pass pass pass The following tests were conducted to demonstrate the advantages of the present coating over the conventional coatings.
Z 15 4 0 ' 7 DN93-176 Two white paint compositions were prepared, a conventional composition using water-reducible, low molecular weight acrylate copolymer as the resin and a composition based on the present invention, which comprises a blend of 40%
by weight of the thernioplastic acrylic polymer in a 70/30 mixture of Isopropyl alcohol and water with the water-soluble acrylic polymer.
Both these compositions utilized Triton CF-10 non-ionic alkylaryl polyether supplied by The Industrial Chemical Division of Union Carbide Chemical and Plastic Co. Triton CF-10 non-ionic alkylaryl polyether is supplied as a liquid and it is utilized as a low foaming wetting agent for pigments used in latex paints.
Both the compositions were pigmented with the white Ti-pure R-900 titanium dioxide pigment supplied by duPont de Nemours Co. Inc., Wilmington, Delaware.
The conventional composition further included metallic dryers at 0.15 parts by weight of cobalt naphthenate and 0.20 parts by weight of manganese naphthenate supplied by Tenneco Chemicals Inc.
Table 5 below sumznarizes the composition on a weight percentage basis.
Table 5 Component of the Conventional The present invention composition composition composition ------------------ ------------------ ------------------water-reducible, low 37.92 ----molecular weight acrylate copolyiner 40% thermoplastic acrylic ---- 40.90 polymer in 70/30 IPA/Water water-soluble acrylic ---- 4.50 polymer Isopropyl alcohol ---- 4.50 Triton @ CF-10 1.07 1.13 Ti-Pure R-900 titanium 15.77 15.77 dioxide pigment 70/30 IPA/Water 44.89 33.20 Dryer 0.35 ----TOTAL 100% 100%
~,~.,~.. ......-..~.,.~,~..~,.~.~ . _ _ ~_.
1 1 N~ OLi? DN93-176 Both conlpositions were applied as a coating having 25.4 rnicrons (1.0 mil) 2.5 microns (0.10 mils) dry film thickness over steel panels. I'he specifications of the coating from both of these compositions is outlined in Table 6 below:
Table 6 Specifications Conventional coating Present invention coating ------------- ------------------ ---------------Weight of solids 39.59 34.54 Pigment/binder ratio 0.69 0.89 Pigment Volume 15.76 21.08 Concentration VOC in lbs/gallon 5.40 5.70 72 hours later the coated steel panels were tested, under the identical ambient conditions. The summary of the test results is outlined in Table 7 below:
Table 7 Tests Conventional coating Present invention coating ---------------- ------------------ -----------------Dry to Touch (DTT) in 20-25 minutes in 10-15 minutes 60 degree gloss 80 85 20 degree gloss 50 65 Adhesion (over B-1000) 10 10 Hardness 2B-B HB-F
Water resistance 5B (soft) HB (no effect) Alkali resistance (1 hr) failed HB (no effect) Alkali resistance (2 hrs) failed HB (no effect) Alkali resistance (3 hrs) failed HB (no effect) Alkali resistance (4 hrs) failed very few blisters Water immersion 5B 2B
Wet adhesion 1.0 1 (Immediate) Wet adhesion (2 hrs 10 10 recovery) The foregoing Table 7 shows that the cured coating made from the present invention provides iniprovement over conventional coating in the following areas:
1. Faster dry to touch time;
2. Improved 20 and 60 degree gloss;
OF
Hoinayoun Jamasbi FOR
AQUEOUS FAST DRYING AEROSOL COATING COMPOSITION
This invention generally relates to aqueous, also known as water-based, aerosol coating compositions and, more particularly, to a gloss-controlled aerosol coating composition having improved drying capability, hardness and alkali resistance over current water-based systenls.
Aerosol paint coinpositions that employ volatile organic solvents as a carrier and propellant for film-forming polymers are known and widely used.
However, the presence of organic solvents in aerosol compositions raise serious environmental concerns due to their toxic nature. Moreover, since such organic solvents are highly flammable, they create hazardous workplace conditions. While aqueous aerosol paint compositions have had some impact in resolving the problems of toxicity and flammability, a continuing concern is the longer drying times typically observed in water-based systems when coinpared to the faster drying times of organic solvent-based aerosol systems.
Furthermore, high gloss aerosol paint compositions, which are typically solvent based, are generally not suitable for coating solvent-sensitive surfaces, such as the surfaces of leather substrates. The present invention addresses this problem by providing for high gloss aerosol paint compositions that do not damage or mar such underlying solvent-sensitive substrate surfaces.
A variety of polymers sucli as acrylics, alkyds, epoxy esters, and vinyl polymers and copolymers may be used in aqueous aerosol compositions as film-forming polymers, which are also known as film formers. Water-based aerosol paint formulations having a mixture of dimethyl ether, water and a water-soluble solvent, such as monohydric alcohol, as a carrier and a propellant are known. The dimethyl ether-based propellant system is said to provide for water-soluble (WS) polymers and water-dilutable [also known as water-reducible (WR)] emulsion polymers that are useful as film-forming polymers.
U.S. Pat. No. 4,450,253 (the Suk patent) describes a film-forming polymer comprising an oil-modified acrylic ester polymer rendered water-soluble by neutralization witli a base, such as ammonia or an amine. This film-forming polymer is applied to a substrate by eniploying a single phase, water-based carrier and propellant system having dimethyl ether, water and water-soluble polar organic solvents. The Suk patent at column 6, lines 56 through 64 erroneously identified a Rohm and Haas Company product, Acrysol WS-24 1) 2 1 t5 4 0 ~J' 7 DN93-176 acrylic dispersion resin as an oil-nlodified acrylic acid ester suitable as a film-forming polymer. This is an erroneous identification of the chemical composition of Acrysol't WS-24 acrylic dispersiort resin, which is typically supplied at 36 % solids in water and is not oil-modified. Also, it is not oil-modified in any variation of the invention as described in the Suk patent.
Furthermore, there is no suggestion in the Suk patent that an acrylic dispersion resin, not modified by oil, can be employed as a film-forming polymer. However, a critical aspect of the invention in the Suk patent is to film-forming polymers that must be oil-rnodified ester polymers which are solubilized and dissolved in the liquid phase propellant-solvent solution provided by the dimethyl ether, water and at least one polar solvent, such as monohydric alcohol, (Specification, column 5, lines 32 through 37). Therefore, since Acrysol WS-24 acrylic dispersion resin is not oil-modified its identification as a drying oil-modified polymer was in error.
The present invention is directed to an aqueous aerosol coating composition comprising a thermoplastic acrylic polymer solubilized in an aqueous solution of a monohydric alcohol to form a solubilized acrylic solution, the thermoplastic acrylic polymer having a weight average molecular weight in the range of 105,000 to 200,000.
The aqueous aerosol coating composition further comprises a blend of the solubilized acrylic solution with a controlling amount of a water-based acrylic polymer for providing a desired degree of gloss and alkali resistance, the water-based acrylic polymer being selected from the group consisting of a water-soluble acrylic polymer, water-reducible acrylic polymer and a combination thereof.
The present invention is also directed to a rnethod of producing an aqueous coating composition comprising, adding a monohydric alcohol to water form an aqueous solution, solubilizing a thermoplastic acrylic polymer having a weight average molecular weight in the range of 105,000 to 200,000 in the aqueous solution to form a solubilized acrylic solution, blending a controlling amount of a water-based acrylic polymer with t11e solubilized acrylic solution to provide a desired degree of gloss and alakli resistance to a coating resulting from the aqueous coating composition.
While aqueous-based carrier and propellant systems have made some improvements over organic solvent-based systerns, furthei- improvements in drying time as measured by set-time, dry-to-touch time and tack-free time are required. The present invention addresses the problems of longer drying times typically observed in conventional aqueous aerosol systems, which utilize oil modified acrylics as film formers.
The present invention furtller provides for environmentally safe aqueous aerosol coating compositions which produce coatings having improved alkali resistance, hardness and gloss that equals or exceeds one normally seen in coatings employing solvent-based aerosol systems.
Generally, monohydric alcollols do not solubilize acrylic polymers, such as, poly(methyl methacrylate) [PMMA]. However, it llas been unexpectedly discovered that certain thermoplastic polymers and copolymers of esters of the methacrylic acid, solubilize in certain mixtures of alcohol and water.
Compared to other organic solvents, these solutions dry rapidly at room temperature, to produce hard and tough films. Thermoplastic acrylic polymers, as defined herein, are those 100 % solid thernloplastic acrylic polymers produced as powders or pellets. A wide variety of thernloplastic acrylic polymers including polymers as well as copolymers, described below, are suitable as film formers in the aerosol compositions of the present invention.
These thermoplastic acrylic polymers are provided with a weight average molecular weight in the range of 105,000 to 200,000, preferably in the range of 105,000 to 120,000 and most preferably 105,000. The weight average molecular weight, as defined herein, is the mean of the weight relative molecular weights of the weight fractions as describeci on pages 6-10, Chapter II of The Characterization of Polymers published by Rohm and Haas Company, Philadelphia, Pennsylvania in 1976. The weight average molecular weights are determined by gel permeation chromatography as described on page 4, Chapter IV of The Charncterization of Polymers published by Rohm and Haas Company, Philadelphia, Pennsylvania in 1976, utilizing polymetllyl methacrylate as the standard.
These thermoplastic acrylic polymers exhibit a glass transition temperature (Tg) varying from 35~ C to 105~ C, preferably from 35 C to 40 C
and most preferably 40* C. The Tg is defined as that temperature at which the properties of the polymer, sucli as, viscosity, impact resistance, hardness, undergo substantial changes. The 'Tg of the acrylic polymer is calculated by substituting the weight percentages and the Tgs of the monomeric components of the acrylic polymer in the well known Fox Equation described in Bulletin of American Physics Society, Vol. 1, Issue 3, page 123 (1956) and on pages 20-21, Chapter IV of The Characterization of Polymers published by Rohm and Haas Company, Philadelphia, Pennsylvania in 1976.
The thermoplastic acrylic polymers suitable for use in the aerosol composition df the present invention have an acid number in the range of 2 to 12, preferably in the range of 3 to 4. The acid number, as defined herein, is a 4 ~~~~~ ~7 DN93-176 number expressed as milligrams of potassium hyciroxide divided by grams of the neutralized polymer.
These thermoplastic acrylic polymers may be prepared by well known polymerization techniques, such as, suspension polymerization and emulsion polymerization of ethylenically unsaturated monomers. Suspension polymerization is preferred. The acrylic content results from the polymerization of acrylate or methacrylate esters, sucli as, for example, methyl acrylate, ethyl acrylate, butyl acrylate, methyl methacrylate, ethyl methacrylate, butyl methacrylate, i-butyl methacrylate, acrylic acid, ulethacrylic acid, and acryloxypropionic acid. The thermoplastic acrylic polymers are preferably prepared by suspension polynlerizing ethyl methacrylate and methacrylic acid or methyl methacrylate, etllyl acrylate and methacrylic acid, the former being the most preferred.
Among the commercially available thermoplastic acrylic polymers suitable for use herein are those made by Rohm and Haas Company, Philadelphia, Pennsylvania, under the trademark AcryloidU solid grade acrylic resins, which are available in 100% solid powder or pelletized form.
These thermoplastic acrylic polymers are solubilized, preferably at room temperature, in a previously prepared aqueous solution of monohydric alcohol, such as isopropanol, n-butanol or 3A alcohol (by weight-95% ethanol and 5%
isopropanol) to fornl a solubilized acrylic solution. Isopropanol is preferred.
The aqueous solution is produced by dissolving by weight 60% to 95%, preferably 70% monohydric alcohol in water. The term "solubilized" as defined herein means "dissolved" or "go in solution." It is desirable to dissolve monohydric alcohol in water before solubilizing the thermoplastic acrylic polymer therein. Such a step appears to prevent the alcohol from swelling the polymer and causing haze in the resulting aqueous solution.
Table 1 below provides the solubility data obtained by solubilizing 40% by weight of the thermoplastic acrylic polymer in various monohydric alcohols at various alcohol to water weight ratios:
Table 1 Alcohol/water N-butanol 3A alcohol (95%
ethanol, 5% IPA) 50/50 Insoluble Insoluble 60/40 Partially soluble Insoluble 70/30 Soluble Partially soluble 80/20 Soluble Partially soluble 90/10 Soluble Soluble 100% Alcohol Insoluble Insoluble S 15110 5 r DN93-176 The weight percentage of the thermoplastic acrylic polymer being solubilized in the aqueous solution of monohydric alcohol is adjusted in accordance with the desired drying rate of the resultant coating. By lowering the weight percentage of the solubilized thermoplastic acrylic polymer, faster drying rates of the resultant coating composition are achieved. The weight percentage of the thermoplastic acrylic polymer solubilized in the aqueous solution of monohydric alcohol and water may be varied from 5% to 45%, preferably from 30% to 40%, most preferably at 40%, all in the weight percentage of the solubilized acrylic solution.
Table 2 below provides the solubility range of the thermoplastic acrylic polymer (Resin) solubilized at various isopropanol (IPA) to water weight ratios:
Table 2 IPA/Water 30% solid Resin 40% solid Resin 50% solid Resin 50/50 Insoluble Insoluble Insoluble 60/40 Insoluble Insoluble Insoluble 70/30 Soluble Soluble Soluble 80/20 Soluble Soluble Soluble 90/10 Soluble Soluble Soluble 100% IPA Insoluble Insoluble Insoluble The appearance of the coating resulting from the foregoing aerosol coating composition is flat. However, the gloss of the resultant coating may be varied by blending the solubilized acrylic solution. with a controlling amount of a water-based acrylic polymer. The "controlling amount" is defined as the amount of water-based acrylic polymer in weight percentage sufficient to achieve a desired degree of gloss and alkali resistance to a coating resulting therefrom. By increasing the amount of the water-based polymer blended with the solubilized acrylic solution, one is able to achieve a more glossy coating.
The water-based acrylic polymers suitable for use in the present invention comprise a water-soluble acrylic polymer, a water-reducible acrylic polymer or a combination of the two. The water-soluble acrylic polymer is preferred.
The water-soluble acrylic polymer suitable for use in the present invention is provided with a weight average molecular weight in the range of 20,000 to 250,000, preferably 200,000, as determined by gel permeation chromatography, based on poly methyl methacrylate as the standard, an acid number typically in the range of 30 to 160, preferably 100 and a Tg in the range of 30 C to 140 C, preferably 45 'C. The water-soluble acrylic polymer comprises from about 40%
to 60% Butyl acrylate and 20% to 40% methyl nlethacrylate and with lower levels of styrene and methyl acrylate. The desired degree of gloss and alkali resistance on the coatings produced from the aerosol coating composition of the present 6 9w It 5 4 0 5) 7 DN93-176 invention is obtained by blending by weight 2% to 12%, preferably 8%, of the water-based acrylic polymer with the solubilized acrylic solution. These weight percentages are based on the total weight of the blend comprising the water-soluble acrylic polymer and the solubilized acrylic solution.
A number of water-soluble acrylic polymers sold by Rohm and Haas Company, under the trademark known as Acrysol@ acrylic dispersion resins are suitable for use in this invention.
As stated earlier, the water-based acrylic polyiner may comprise a water-reducible, low molecular weight acrylate copolymer having copolymerized units of an alkyl acrylate and an alkyl methacrylate, wherein the alkyl group has 3 to 5 carbon atoms. The preferred copolymers comprise 5% to 20 % butyl acrylate and from 30% to 60 % isobutyl methacrylate by weight. In addition, the composition may comprise 10% to 30 % by weight of a copolyn-ierized drying oil, such as, linseed oil, soya oil, tung oil, sunflower oil or other polyunsaturated oils.
Finally, the composition may comprise 10% to 20 % by weight of olefinically unsaturated acid, or acid anhydride, such as acrylic acid, methacrylic acid, maleic acid and the like or an anhydride thereof. The weight average molecular weight of the copolymer is in the range of 300 to 20,000, preferably from 6000 to 12,000 and most preferably from 8000 to 10,000. The desired. clegree of gloss and alkali resistance on the coatings produced from the aerosol coating composition of the present invention is obtained by blending by weight 2% to 30%, preferably 8%, of the water-reducible, low molecular weight acrylate copolymer with the solubilized acrylic solution. These weight percentages are based on the total weight of the blend comprising the water-reducible, low molecular weight acrylate copolymer and the solubilized acrylic solution.
A water-reducible, low molecular weight co-polymer of butyl acrylate and isobutyl methacrylate having a weight average molecular weight of 9000 is most preferred.
As stated earlier, the water-based acrylic polymer may comprise a combination of water-soluble and water-reducible acrylic polymers. In order to form such a combination, the water-reducible acrylic polymer is neutralized and the viscosity reduced with water to prevent precipitation of the polymer.
The neutralization can occur before or after the dryers are added to the polymer but typically before reduction with water. After water is adcled, the water-soluble acrylic polymer can be added to form the combination. If the above order of addition is not adliered to, it would be more difficult to form the combination of water-soluble and water-reducible acrylic polymers.
The weight ratio of the water-soluble acrylic polymer to the water-reducible, low molecular weight copolymer should be 20/80 to 80/20, while the 7 I o d~ DN93-176 preferred weight ratio should be from 40/60 to 60/40. When weight ratios are outside of the above ranges, the combinations are less stable and the coatings produced therefrom are inferior.
The present invention contemplates an aerosol composition adopted for providing a continuous film on a sulistrate upon discllarge frorn suitable containment means, such as, for example, an aerosol can. The propellant-active carrier system employed in the present invention preferably includes dimethyl ether and water. Dimethyl ether is a colorless, stable, polar liquid with a boiling point of minus 25 C. The aerosol composition of the present invention may comprise from 5 % to 60 %, preferably from 25 % to 50 % of dimethyl ether by weight, based on the total weight oE the aerosol composition.
While it is preferred that dimethyl ether is the sole propellant, under some circumstances, however, 0 % to up to 50 % by weight of dimethyl ether may be replaced by another liquid propellant, such as, an aliphatic llydrocarbon or a fluorinated hydrocarbon. Further, if desired, a gaseous propellant, such as nitrogen, carbon dioxide, nitrous oxide, may also be used.
Water is present in the composition of the present invention in an amount varying from 10 % to 70 %, preferably varying from 20 % to 60 % by weight of the total weight of the aerosol paint composition.
The aerosol coating composition of the present invention may further include, additives, such as a surfactant, pigment, pH stabilizer, antifoam agent, plasticizer, drying agents. In general, there will be less than 20 %, preferably less than 15 % by weight, based on the total weight of the composition, of the pigment. Suitably, the remaining foregoing additives, when present, would not exceed 3 % by weight, based on the total weight of the composition, for each additive, and usually only up to 1'I~, or 2% of each other adctitive would be present.
A blend of a thermoplastic acrylic polymer solubilized in a previously prepared aqueous solution of a monohydric alcollol with a water-based acrylic polymer in a water-based carrier and propellant system having dimethyl ether and water provides paiilt compositions with the desired film-forming and drying properties that are not obtained when the water-reducible, low molecular weight copolymer is einployed without the water-soluble acrylic polymer. Coating properties are further enhanced, when the water-reducible low molecular weight polymer undergoes air cure.
The present coating composition is suitable for use in many coating applications, such as, f'or example, wood finishes, printing inks, coatings on solvent sensitive substrates, such as, leather, sealers, over print varnishes, label varnishes, paper coatings, floor finishes, ceramic binders, vacuum metallized FW~ 5 4 0 5 7 coatings, coatings over polymeric substrates, traffic and zone marking paints, glaze coatings, wall coatings, clear coatings on delicate substrates, such as those of art objects.
The following test procedures were employed in evaluating the physical and chemical properties of the foregoing aerosol coating compositions. Unless and otherwise stated, all the tests were conducted under the standardized procedures developed by The American Society of Testing Materials, (ASTM), Philadelphia, Pennsylvania.
TEST PROCEDURES
- Dry to Touch time ......................ASTM D-1640 - Gloss ..............................................ASTM D-523 (The 20 degree and 60 degree gloss were measured with glass meters manufactured by the Gardner Instrument Company).
- Pencil Hardness ..........................ASTM D-1737 (6H being the hardest pencil and 6B being the softest pencil) - Cross Hatch Adhesion ...............ASTM D-3359 (on the scale of 1 through 10, 1 represents poor adhesion and 10 represents no loss of adhesion) - Water resistance ....................................A spot of water was left on the coated surface for a specified length of time. Pencil hardness was measured at the start and at the end of the test.
- Alkali resistance ...........................A spot of 7% solution of NH4OH
was left on the coated surface for a specified length of time. Appearance was checked at the start and at the end of the test.
- Water immersion .........................A coated panel was immersed in water for 2 hours. Pencil hardness was measured at the start and at the end of the test.
- Wet adhesion ................................Cross hatch adhesion was measured immediately after the coated panel was removed from the water immersion test described above. Another cross hatch adhesion was measured 2 hours later.
Some embodiments of the invention will now be described in detail in the following examples.
The three clear water-based compositions were prepared as follows:
85 parts by weight of isopropyl alcollol was dissolved in 15 parts by weight of deionized water to form an aqueous solution. Isopropyl alcohol @ 91%
strength with a flash point of 18 C , vapor pressure of 34 mm Hg at 20 C and a specific gravity of 0.818 at 20 C supplied by Union Carbide Inc., was used.
100%
9 21 ~4 0 5r 7 DN93-176 solid pellets of the thermoplastic acrylic polymer were then dissolved in the the aqueous solution at 40% by weight of the solution.
To the above described solution, water-reducible, low molecular weight copolymer at three different strengths, namely 27%, 19% and 0% by weight, was added to analyze the effect of the water-reducible, low molecular weight copolymer on gloss, adhesion, alkali resistance, and water spot effect on the coating resulting therefrom.
Table 3 below provides the composition of the three sample formulations.
Table 3 COMPONENTS Sample A Sample B Sample C
40% solution of the thermoplastic 12% 20% 39%
acrylic polymer in 85/15 IPA/Water water-reducible, low rnolecular 27% 19% 0%
weight acrylate copolymer 85/15IPA/Water 61% 61 h 61%
TOTAL 100% 100% 100%
Each of these sample formulations were tested for 60 degree gloss, cross hatcli adhesion, alkali resistance (2 hours), and water resistance (2 hours).
Adhesion of 10 demonstrates the best adhesion. It is clear from Table 4, below, that there is a direct relationship between the amount of the water-reducible, low molecular weight acrylate copolymer present in the formulation and the resulting gloss of the overall system, i.e., as the amount of the water-reducible, low molecular weight acrylate copolymer is increased, the gloss of the coating resulting therefrom is also improved.
Table 4 TESTS Sample A Sample B Sample C
60 degree gloss 90+/-2 70+/-2 50+/-2 Adhesion 10 10 10 Alkali resistance (2 hrs) fail fail pass Water resistance (2 hrs) pass pass pass The following tests were conducted to demonstrate the advantages of the present coating over the conventional coatings.
Z 15 4 0 ' 7 DN93-176 Two white paint compositions were prepared, a conventional composition using water-reducible, low molecular weight acrylate copolymer as the resin and a composition based on the present invention, which comprises a blend of 40%
by weight of the thernioplastic acrylic polymer in a 70/30 mixture of Isopropyl alcohol and water with the water-soluble acrylic polymer.
Both these compositions utilized Triton CF-10 non-ionic alkylaryl polyether supplied by The Industrial Chemical Division of Union Carbide Chemical and Plastic Co. Triton CF-10 non-ionic alkylaryl polyether is supplied as a liquid and it is utilized as a low foaming wetting agent for pigments used in latex paints.
Both the compositions were pigmented with the white Ti-pure R-900 titanium dioxide pigment supplied by duPont de Nemours Co. Inc., Wilmington, Delaware.
The conventional composition further included metallic dryers at 0.15 parts by weight of cobalt naphthenate and 0.20 parts by weight of manganese naphthenate supplied by Tenneco Chemicals Inc.
Table 5 below sumznarizes the composition on a weight percentage basis.
Table 5 Component of the Conventional The present invention composition composition composition ------------------ ------------------ ------------------water-reducible, low 37.92 ----molecular weight acrylate copolyiner 40% thermoplastic acrylic ---- 40.90 polymer in 70/30 IPA/Water water-soluble acrylic ---- 4.50 polymer Isopropyl alcohol ---- 4.50 Triton @ CF-10 1.07 1.13 Ti-Pure R-900 titanium 15.77 15.77 dioxide pigment 70/30 IPA/Water 44.89 33.20 Dryer 0.35 ----TOTAL 100% 100%
~,~.,~.. ......-..~.,.~,~..~,.~.~ . _ _ ~_.
1 1 N~ OLi? DN93-176 Both conlpositions were applied as a coating having 25.4 rnicrons (1.0 mil) 2.5 microns (0.10 mils) dry film thickness over steel panels. I'he specifications of the coating from both of these compositions is outlined in Table 6 below:
Table 6 Specifications Conventional coating Present invention coating ------------- ------------------ ---------------Weight of solids 39.59 34.54 Pigment/binder ratio 0.69 0.89 Pigment Volume 15.76 21.08 Concentration VOC in lbs/gallon 5.40 5.70 72 hours later the coated steel panels were tested, under the identical ambient conditions. The summary of the test results is outlined in Table 7 below:
Table 7 Tests Conventional coating Present invention coating ---------------- ------------------ -----------------Dry to Touch (DTT) in 20-25 minutes in 10-15 minutes 60 degree gloss 80 85 20 degree gloss 50 65 Adhesion (over B-1000) 10 10 Hardness 2B-B HB-F
Water resistance 5B (soft) HB (no effect) Alkali resistance (1 hr) failed HB (no effect) Alkali resistance (2 hrs) failed HB (no effect) Alkali resistance (3 hrs) failed HB (no effect) Alkali resistance (4 hrs) failed very few blisters Water immersion 5B 2B
Wet adhesion 1.0 1 (Immediate) Wet adhesion (2 hrs 10 10 recovery) The foregoing Table 7 shows that the cured coating made from the present invention provides iniprovement over conventional coating in the following areas:
1. Faster dry to touch time;
2. Improved 20 and 60 degree gloss;
3. Increased hardness; and 4. Improved alkali resistance.
Claims (8)
1. An aqueous aerosol coating composition comprising a thermoplastic acrylic polymer solubilized in an aqueous solution of a monohydric alcohol to form a solubilized acrylic solution, said thermoplastic acrylic polymer having a weight average molecular weight in the range of 105,000 to 200,000, an acid number in the range of from 2 to 12, and is polymerized from ethylenically unsaturated monomers, wherein said composition further comprises a controlling amount of a water-based acrylic polymer for providing a desired degree of glass and alkali resistance, the said water-based acrylic polymer being selected from the group consisting of a water-soluble acrylic polymer, a water-reducible acrylic polymer and a combination thereof.
2. The composition of claim 1 wherein said solubilized acrylic solution comprises 5% to to 45% by weight of said thermoplastic acrylic polymer.
3. The composition of claim 1 wherein said thermoplastic acrylic polymer has a Tg in the range of 35°C to 105°C.
4. The composition of claim 1 wherein said aqueous solution comprises 60% to 95% by weight of said monohydric alcohol selected from the group consisting of isopropanol, n-butanol and 3A alcohol.
5. The coating composition of claim 1 wherein the said water-based acrylic polymer is a water-soluble acrylic polymer, the said controlling amount of said water-soluble acrylic polymer is in the range of 2% to 12% by weight of the said acrylic polymer solubilized in aqueous solution and the water-soluble acrylic polymer and wherein said water-soluble acrylic polymer is an acrylic polymer having a weight average molecular weight in the range of 20,000 to 200,000, a Tg in the range of 30°C to 140°C and an acid number in the range of 30 to 160.
6. The composition of claim 1 further comprises less than 20% by weight of a pigment and less than 3% by weight of a surfactant, pH stabilizer, antifoam agent, plasticizer, drying agent or a combination thereof.
7. A coating of the composition of claim 1 on the surface of a substrate.
8. A method of producing an aqueous coating composition comprising:
adding a monohydric alcohol to water to form an aqueous solution;
solubilizing a thermoplastic acrylic polymer having a weight average molecular weight in the range of 105,000 to 200,000 in said aqueous solution to form a solubilized acrylic solution; and blending a controlling amount of a water-based acrylic polymer with said solubilized acrylic solution to provide a desired degree of gloss and alkali resistance to a coating resulting from said aqueous coating composition.
adding a monohydric alcohol to water to form an aqueous solution;
solubilizing a thermoplastic acrylic polymer having a weight average molecular weight in the range of 105,000 to 200,000 in said aqueous solution to form a solubilized acrylic solution; and blending a controlling amount of a water-based acrylic polymer with said solubilized acrylic solution to provide a desired degree of gloss and alkali resistance to a coating resulting from said aqueous coating composition.