CN102660168A - Granite-simulated coating and preparation method thereof - Google Patents
Granite-simulated coating and preparation method thereof Download PDFInfo
- Publication number
- CN102660168A CN102660168A CN2012101750025A CN201210175002A CN102660168A CN 102660168 A CN102660168 A CN 102660168A CN 2012101750025 A CN2012101750025 A CN 2012101750025A CN 201210175002 A CN201210175002 A CN 201210175002A CN 102660168 A CN102660168 A CN 102660168A
- Authority
- CN
- China
- Prior art keywords
- mass percent
- solution
- preparation
- artificial granite
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a preparation method of granite-simulated coating. The preparation method includes the steps of firstly, preparing base paint; secondly, adding pigments into the base paint for color matching; thirdly, granulating the base paint, forming water insoluble coating films on surfaces of particles of the base paint, and dispersing the particles into an aqueous system; and fourthly, coating the particles with finishing coat to obtain the granite-simulated coating. The invention further discloses the granite-simulated coating. The preparation method is energy-saving, environment-friendly, nontoxic, harmless and simple and safe to operate. Product and construction cost is low, decorative effects of granite can be formed with the coating, and defects of natural stone applied to exterior wall decoration are overcome.
Description
Technical field
The present invention relates to a kind of decorating building and use coating, particularly a kind of preparation method of artificial granite coating and this artificial granite coating.
Background technology
Fast development along with Building Trade in China; People are also increasingly high to the decoration requirement of buildings, and wherein, natural granite has luxurious dignified decorative effect and superior barrier propterty; But cost is relatively more expensive; And tellurian resource is limited, the have to condition that makes resource deficient more in the face of constantly consuming of the mankind, thereby the application of grouan material is limited to.
External wall mainly adopts dry-hang stone and true mineral varnish as finishing material at present.
It is following not enough to adopt the dry-hang stone finishing material to exist, and the deadweight of stone material is bigger, and dry-hang stone can increase the body of wall load; Difficulty of construction is big, cost is higher, dangerous; Particularly in the earthquake disaster process, coming off of stone material is very obvious, and be very big to people's life threat; Carbon dioxide in air, sulfur dioxide gas are dissolved in the rainwater, can corrode the marble stone material, are prone to make it to tarnish; Because stone material has micropore, moisture is to internal penetration, so that anchor bar gets rusty, ooze out iron after, cause rust staining; During wet combining was installed, sheet material contacted with concrete, met aqueous alkaline solution and oozed out stone surface, was prone to make stone material to pollute variable color.
Adopt true mineral varnish finishing material not enough below existing, true mineral varnish is to be filler with the shades of colour crushed stone, and film coated surface is coarse, and is uneven, do not have the feel of lithotome, is prone to dust, laying dust, and anti-fouling performance is relatively poor.
Summary of the invention
The object of the present invention is to provide a kind of preparation method of artificial granite coating and a kind of by the prepared artificial granite coating of this method; Its energy-conserving and environment-protective; Nontoxic, method is operated succinct safety, and product and construction cost are low; Can reach many decorative effects that grouan has, avoid the many defectives that exist in the lithotome decoration of outside wall.
The present invention for realizing the technical scheme that above-mentioned purpose adopted is:
A kind of preparation method of artificial granite coating, it may further comprise the steps:
(1) preparation base paint;
(2) pigment is added in toning in base paint;
(3) granulation makes base paint particulate surface form water-fast coating film, and is scattered in the water-based system with graininess;
(4) coat lacquering, make artificial granite coating.
As further improvement of the present invention, said step may further comprise the steps in (1):
(11) be that 48.2% deionized water joins in the container and stirs with mass percent, in the process that stirs, add mass percent and be 0.5% Natvosol, the rotating speed dispersion of changeing with PM 100 5 minutes forms first solution;
(12) in this first solution, add dispersion agent, skimmer, wetting agent and rubber-emulsion paint multifunction additive in proportion successively, the rotating speed that changes with PM 500 disperseed 5 minutes, formed second solution;
(13) in this second solution, add kaolin and water-ground limestone in proportion successively, and disperseed 15 minutes, form the 3rd solution with 1500 rpms rotating speed;
(14) test the dispersity of the 3rd solution, after dispersity reaches 50 microns, add organosilicon crylic acid latex in proportion, alkali dissolves shape thickening material and skimmer, makes base paint.
As further improvement of the present invention, in the said step (2), in the prepared base paint of above-mentioned steps (14), add mass percent respectively and be 1% black slurry, 2% redness slurry and 2% yellow slurry, form the 4th solution.
As further improvement of the present invention, said step may further comprise the steps in (3):
(31) preparation colloidal solution is to add 0.3% sodium carboxymethylcellulose pyce in 40% the water in mass percent, and stirs always and make this sodium carboxymethylcellulose pyce dissolve fully, and to add mass percent be that 3% lithium magnesium silicate forms colloidal solution;
(32) with colloidal solution and the 4th solution mixing granulation; Make base paint particulate surface form water-fast coating film; And be scattered in the water-based system with graininess, forming the 5th solution, the mass percent of this colloidal solution and the 4th solution is 22.5%: 22.5%.
As further improvement of the present invention, said step may further comprise the steps in (4):
(41) preparation coats emulsion, is 30% organosilicon crylic acid latex, 1.5% film coalescence aid, 17.5% water and 1% mixed with propylene glycol with mass percent, makes this coating emulsion;
(42) lacquering is to mix at 50: 50 with the 5th solution and this coating emulsion by mass percentage, makes artificial granite coating.
As further improvement of the present invention, in the step (12), this dispersion agent is the sodium salt dispersion agent, and its mass percent is 0.4%; This skimmer is skimmer A10, and its mass percent is 0.3%; This wetting agent is wetting agent X405, and its mass percent is 0.1%; This rubber-emulsion paint multifunction additive is AMP-95, and its mass percent is 0.1%; In the step (13), this kaolinic mass percent is 10%; This water-ground limestone is 1250 orders, and its mass percent is 5%; In the step (14), the mass percent of this organosilicon crylic acid latex is 35%; The mass percent that alkali dissolves the shape thickening material is 3%; The mass percent of skimmer is 0.1%.
The prepared artificial granite coating of a kind of preparation method by aforementioned artificial granite coating, its feed composition and mass percent are following:
Base paint 22.5%;
Colloidal solution 22.5%;
Pigment 5%;
Coat emulsion 50.
As further improvement of the present invention, the feed composition and the mass percent of said base paint are following:
As further improvement of the present invention, said colloidal solution comprises that mass percent is 40% water, 0.3% sodium carboxymethylcellulose pyce and 3% lithium magnesium silicate; This pigment comprises that mass percent is 1% black slurry, 2% redness slurry and 2% yellow slurry.
As further improvement of the present invention, said coating emulsion comprises that mass percent is 30% organosilicon crylic acid latex, 1.5% film coalescence aid, 17.5% water and 1% Ucar 35.
Beneficial effect of the present invention: the inventive method energy-conserving and environment-protective, nontoxic, method is operated succinct safety, and product and construction cost are low, can reach many decorative effects that grouan has, and have avoided the many defectives that exist in the lithotome decoration of outside wall.
Embodiment
Embodiment 1: the preparation method of a kind of artificial granite coating of the present invention, and it may further comprise the steps:
(1) preparation base paint;
(2) pigment is added in toning in base paint;
(3) granulation makes base paint particulate surface form water-fast coating film, and is scattered in the water-based system with graininess;
(4) coat lacquering, make artificial granite coating.
Said step may further comprise the steps in (1):
(11) be that 48.2% deionized water joins in the container and stirs with mass percent, in the process that stirs, add mass percent and be 0.5% Natvosol, the rotating speed dispersion of changeing with PM 100 5 minutes forms first solution;
(12) in this first solution, add dispersion agent, skimmer, wetting agent and rubber-emulsion paint multifunction additive in proportion successively, the rotating speed that changes with PM 500 disperseed 5 minutes, formed second solution;
(13) in this second solution, add kaolin and water-ground limestone in proportion successively, and disperseed 15 minutes, form the 3rd solution with 1500 rpms rotating speed;
(14) test the dispersity of the 3rd solution, after dispersity reaches 50 microns, add organosilicon crylic acid latex in proportion, alkali dissolves shape thickening material and skimmer, makes base paint.
In the said step (2), in the prepared base paint of above-mentioned steps (14), add mass percent respectively and be 1% black slurry, 2% redness slurry and 2% yellow slurry, form the 4th solution.
Said step may further comprise the steps in (3):
(31) preparation colloidal solution is to add 0.3% sodium carboxymethylcellulose pyce in 40% the water in mass percent, and stirs always and make this sodium carboxymethylcellulose pyce dissolve fully, and to add mass percent be that 3% lithium magnesium silicate forms colloidal solution;
(32) with colloidal solution and the 4th solution mixing granulation; Make base paint particulate surface form water-fast coating film; And be scattered in the water-based system with graininess, forming the 5th solution, the mass percent of this colloidal solution and the 4th solution is 22.5%: 22.5%.
Said step may further comprise the steps in (4):
(41) preparation coats emulsion, is 30% organosilicon crylic acid latex, 1.5% film coalescence aid, 17.5% water and 1% mixed with propylene glycol with mass percent, makes this coating emulsion;
(42) lacquering is to mix at 50: 50 with the 5th solution and this coating emulsion by mass percentage, makes artificial granite coating.
In the step (12), this dispersion agent is the sodium salt dispersion agent, and its mass percent is 0.4%; This skimmer is skimmer A10, and its mass percent is 0.3%; This wetting agent is wetting agent X405, and its mass percent is 0.1%; This rubber-emulsion paint multifunction additive is AMP-95, and its mass percent is 0.1%; In the step (13), this kaolinic mass percent is 10%; This water-ground limestone is 1250 orders, and its mass percent is 5%; In the step (14), the mass percent of this organosilicon crylic acid latex is 35%; The mass percent that alkali dissolves the shape thickening material is 3%; The mass percent of skimmer is 0.1%.
The prepared artificial granite coating of a kind of preparation method by aforementioned artificial granite coating, its feed composition and mass percent are following:
Base paint 22.5%;
Colloidal solution 22.5%;
Pigment 5%;
Coat emulsion 50.
The feed composition and the mass percent of said base paint are following:
Said colloidal solution comprises that mass percent is 40% water, 0.3% sodium carboxymethylcellulose pyce and 3% lithium magnesium silicate; This pigment comprises that mass percent is 1% black slurry, 2% redness slurry and 2% yellow slurry.
Said coating emulsion comprises that mass percent is 30% organosilicon crylic acid latex, 1.5% film coalescence aid, 17.5% water and 1% Ucar 35.
The inventive method energy-conserving and environment-protective, nontoxic, method is operated succinct safety, and product and construction cost are low, can reach many decorative effects that grouan has, and have avoided the many defectives that exist in the lithotome decoration of outside wall.
Of the embodiment of the invention, with artificial granite coating of the same or similar structure of the present invention and preparation method thereof, all within protection scope of the present invention.
Claims (10)
1. the preparation method of an artificial granite coating is characterized in that, it may further comprise the steps:
(1) preparation base paint;
(2) pigment is added in toning in base paint;
(3) granulation makes base paint particulate surface form water-fast coating film, and is scattered in the water-based system with graininess;
(4) coat lacquering, make artificial granite coating.
2. the preparation method of artificial granite coating according to claim 1 is characterized in that, said step may further comprise the steps in (1):
(11) be that 48.2% deionized water joins in the container and stirs with mass percent, in the process that stirs, add mass percent and be 0.5% Natvosol, the rotating speed dispersion of changeing with PM 100 5 minutes forms first solution;
(12) in this first solution, add dispersion agent, skimmer, wetting agent and rubber-emulsion paint multifunction additive in proportion successively, the rotating speed that changes with PM 500 disperseed 5 minutes, formed second solution;
(13) in this second solution, add kaolin and water-ground limestone in proportion successively, and disperseed 15 minutes, form the 3rd solution with 1500 rpms rotating speed;
(14) test the dispersity of the 3rd solution, after dispersity reaches 50 microns, add organosilicon crylic acid latex in proportion, alkali dissolves shape thickening material and skimmer, makes base paint.
3. the preparation method of artificial granite coating according to claim 2; It is characterized in that; In the said step (2), in the prepared base paint of above-mentioned steps (14), add mass percent respectively and be 1% black slurry, 2% redness slurry and 2% yellow slurry, form the 4th solution.
4. the preparation method of artificial granite coating according to claim 3 is characterized in that, said step may further comprise the steps in (3):
(31) preparation colloidal solution is to add 0.3% sodium carboxymethylcellulose pyce in 40% the water in mass percent, and stirs always and make this sodium carboxymethylcellulose pyce dissolve fully, and to add mass percent be that 3% lithium magnesium silicate forms colloidal solution;
(32) with colloidal solution and the 4th solution mixing granulation; Make base paint particulate surface form water-fast coating film; And be scattered in the water-based system with graininess, forming the 5th solution, the mass percent of this colloidal solution and the 4th solution is 22.5%: 22.5%.
5. the preparation method of artificial granite coating according to claim 4 is characterized in that, said step may further comprise the steps in (4):
(41) preparation coats emulsion, is 30% organosilicon crylic acid latex, 1.5% film coalescence aid, 17.5% water and 1% mixed with propylene glycol with mass percent, makes this coating emulsion;
(42) lacquering is to mix at 50: 50 with the 5th solution and this coating emulsion by mass percentage, makes artificial granite coating.
6. the preparation method of artificial granite coating according to claim 2 is characterized in that, in the step (12), this dispersion agent is the sodium salt dispersion agent, and its mass percent is 0.4%; This skimmer is skimmer A10, and its mass percent is 0.3%; This wetting agent is wetting agent X405, and its mass percent is 0.1%; This rubber-emulsion paint multifunction additive is AMP-95, and its mass percent is 0.1%; In the step (13), this kaolinic mass percent is 10%; This water-ground limestone is 1250 orders, and its mass percent is 5%; In the step (14), the mass percent of this organosilicon crylic acid latex is 35%; The mass percent that alkali dissolves the shape thickening material is 3%; The mass percent of skimmer is 0.1%.
7. prepared artificial granite coating of the preparation method by the said artificial granite coating of claim 1, it is characterized in that: its feed composition and mass percent are following:
Base paint 22.5%;
Colloidal solution 22.5%;
Pigment 5%;
Coat emulsion 50.
8. artificial granite coating according to claim 7 is characterized in that, the feed composition and the mass percent of said base paint are following:
9. artificial granite coating according to claim 7 is characterized in that, said colloidal solution comprises that mass percent is 40% water, 0.3% sodium carboxymethylcellulose pyce and 3% lithium magnesium silicate; This pigment comprises that mass percent is 1% black slurry, 2% redness slurry and 2% yellow slurry.
10. artificial granite coating according to claim 7 is characterized in that, said coating emulsion comprises that mass percent is 30% organosilicon crylic acid latex, 1.5% film coalescence aid, 17.5% water and 1% Ucar 35.