CN1301277A - 纳米模具和纳米薄膜及使用水溶性前体制备纳米模具和纳米薄膜的方法 - Google Patents
纳米模具和纳米薄膜及使用水溶性前体制备纳米模具和纳米薄膜的方法 Download PDFInfo
- Publication number
- CN1301277A CN1301277A CN99806344A CN99806344A CN1301277A CN 1301277 A CN1301277 A CN 1301277A CN 99806344 A CN99806344 A CN 99806344A CN 99806344 A CN99806344 A CN 99806344A CN 1301277 A CN1301277 A CN 1301277A
- Authority
- CN
- China
- Prior art keywords
- group
- film
- composition
- alcohol
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种制备组合物的方法,该组合物是用来制备纳米模具和纳米薄膜的,包括:在导致物质(进一步)水解的条件下,让选自硅和主族及副族金属元素化合物的水溶胶和/或醇溶胶,与具有可水解的烷氧基物质(至少包括一种有机改性烷氧基硅烷或由它而得到的预缩合物)接触,然后将所产生的醇或原来就任意存在的醇全部除去。本发明的特征在于,醇被充分地除去,使其在组合物中剩余量不超过20%(重量)。
Description
本发明涉及纳米模具(nanostructured forms)和纳米薄膜及通过稳定的水溶性前体制备纳米模具和纳米薄膜的方法,特别是适合于光学用途的纳米模具和纳米薄膜。
在文献中,已经描述了为涂覆目的,用含水前体制备透明材料(包括有机/无机复合材料)的方法。
特别是JP-A-53-6339,描述了一种复合材料的合成方法,即从具有反应活性的有机改性硅烷和惰性的有机改性硅烷开始,并在含水硅溶胶和磷酸(作为催化剂)的存在下进行水解。没有除去在缩合反应中所形成的醇。
JP-A-63-37168描述了一种复合材料的合成方法,即从分散于含水介质中的可进行自由基交联的丙烯酸酯基单体和有机改性硅烷开始,这些硅烷的有机自由基,在胶状二氧化硅和非离子表面活性剂的存在下,可同样地构成自由基交联体系。水解和缩合反应在不同的过程步骤中进行。这里也没有除去在缩合反应中所形成的醇。
JP-A-36-37167中,描述了一种类似的体系,其中的硅烷具有阳离子性的可交联自由基。
US-A-5411787描述了一种复合材料的合成方法,即从分散于水中的聚合粘合剂、至少一种氨基硅烷组分和尺寸低于20nm的胶状微粒开始。在这种情况下,也没有除去由硅烷水解所形成的醇。
US-A-4799963描述了硅烷基复合材料的制备方法,其中额外混入了胶状的二氧化硅或纳米级的氧化铈。
所引用的参考文献不包含任何有关作用机制的说明,也没有他们所描述的体系贮存期限的信息。同样,在大多数情况下,缺乏有关剩余溶剂含量的信息,尽管在合成方法的数学再加工中建议,剩余溶剂含量按体积计不超过10%。
以所述的现有文献为基础所进行的研究指出,通过控制具有功能性硅烷的胶状体系的涂覆,可以降低水敏感性,也就是改善水解和缩合反应;并且这种体系可用于制备稳定的体系,以生产模具和薄膜,尤其是适用于工业中应用的模具和薄膜。
因此,本发明的目的是提供一种通过稳定的水溶性中间体制备纳米模具和薄膜的方法,特别是适用于光学用途的纳米模具和薄膜的方法。
根据本发明,现发现,可以通过涂覆来使用具有活泼的单聚体或低聚体组分(硅烷或其预缩合物)并经过静电处理而稳定化的(因此而极其浓度敏感)含水胶状悬浮液;而且在浓缩过程中,该悬浮液因此而不表现出Stern(Z.Elektrochem.,508(1924))所描述的效应,即两个带有同种电荷的微粒互相接近时的聚集效应;并不表现出化学反应,而在其它情况下,两个具有活泼表面基团的微粒之间的化学反应是自发地进行的。通过除去(在减压下进行)缩合反应中所生成的醇(一般是甲醇或乙醇),实现浓缩和反应平衡向产物一侧移动,同时生成表面缩合物,从而就得到了缩合物的非常高的贮存稳定性(大于14天)和相对较低的剩余溶剂含量(按重量计,一般不超过20%,具体地讲,不超过10%)的结合。
由于表面改性剂与微粒之间的化学键(例如氢键或金属-氧键(-Al-O-Si-、-Ti-O-Si-等,参见Chem.Mat.7(1995),1050-52))的可逆性,如果加热,上面所述的过程就向相反的方向进行,因此微粒是可以交联并固化的。还可以通过适当地选择表面改性剂上面的有机基团,发生进一步的反应(例如这些有机基团之间互相发生的反应)。
这样就可以使水溶胶(如勃母石、TiO2、ZrO2或SiO2溶胶,以及周期表中的主族和过渡金属化合物的其它水溶胶)与有机改性硅烷按这样的方式发生反应,即脱除溶剂(如果需要)然后将剩下的液体分散于水中,得到稳定时间较长的澄清溶液。为了使微粒与有机改性烷氧基硅烷的涂覆反应进行到这样的程度,即产生水解和缩合均稳定的液体体系,脱除溶剂(醇)是必需的。用通常的技术,就可以将这些体系用于涂覆,这取决于有机改性烷氧基硅烷上面的官能团;如果需要,可借助于合适的催化剂进行热固化或光化学固化。在热固化的情况下,形成无机网状交联;如果所用的有机基团合适,还形成与无机网状交联平行的有机交联。所合成的纳米复合材料因其高透明度而著名。如果将其用作薄膜,对很多种基材,它们均展示良好的粘合性和极高的抗划伤性。
因此,本发明提供一种制备组合物的方法,并用该组合物制备纳米模具和薄膜,该方法包括:在导致物质(进一步)水解的条件下,让选自硅和主族及副族金属元素化合物的水溶胶和/或醇溶胶,与具有可水解的烷氧基物质(至少包括一种有机改性烷氧基硅烷或由它而得到的预缩合物)接触;然后将所产生的醇或原来就任意存在的各种醇除去,并且特征在于,除去这样数量的醇,以使组合物的剩余醇含量不超过20%(重量),优选不超过15%(重量),特别是不超过10%(重量)。
本发明还提供通过上述方法所获得的组合物,并用这些组合物制备纳米模具和带有纳米薄膜的基材。
本发明的方法不同于现有技术的类似方法,具体地讲是由于这样的事实,即除去体系中存在的大部分溶剂(醇)。这使水解和缩合平衡向产物一侧移动,并使相应的液体体系稳定化。一般地,对烷氧基水解所形成的醇,至少其理论产量(按重量计)的30%,特别是50%,最好是70%要被除去。特别优选至少80%(重量),更优选90%(重量)的这种醇要被除去。这种计算不包括任何原来就存在的醇(例如来自溶胶原料的醇;假设这种醇被100%除去),但包括在制备所用预缩合物的过程中就已生成的醇。因此,总体上保证硅烷中存在的可缩合(水解的)基团有10-80%(优选20-50%)发生缩合反应。
最好在减压下将醇从反应体系中移出,以避免体系的过量热载荷。一般地,将醇移出体系时的温度不应超过60℃,具体地不应超过50℃,优选不应超过40℃。
在下文中,我们更详细地描述用于本发明方法的原料。
所用的溶胶可以是水溶胶、醇溶胶或水/醇溶胶。优选使用简单的水溶胶。如果使用含醇溶胶,那么所述的醇最好具有1-4个碳原子,也就是甲醇、乙醇、丙醇、异丙醇或一种丁醇。
本发明的溶胶包含选自硅和主族及过渡金属的一种或多种元素的一种或多种化合物(优选一种化合物)。优选的主族和过渡金属包含周期表中的第三和第四主族的金属(特别是Al、Ga、Ge和Sn),以及第三至第五副族的金属(特别是Ti、Zr、Hf、V、Nb和Ta)。其他可导致良好结果的金属化合物,如Zn、Mo和W的化合物,也是可以选择的。
优选的相应的元素化合物包含氧化物、氢氧化氧化物、硫化物、硒化物或磷酸盐,特别优选氧化物、氢氧化氧化物。因此,本发明所用溶胶中的化合物具体地(优选地)包含SiO2、Al2O3、AlOOH(特别是勃母石)、TiO2、ZrO2及它们的混合物。
用于本发明方法的溶胶所具有的固含量,按重量计一般为5-50%,优选10-40%,特别优选15-30%。
用于本发明方法的含可水解烷氧基的物质,包括至少一种有机改性烷氧基硅烷和/或由其衍生而来的预缩合物。用于本发明的有机改性烷氧基硅烷,优选具有结构式(Ⅰ)的有机改性烷氧基硅烷:
R′4-xSi(OR)x (Ⅰ)其中基团R之间是相同的或不同的(优选相同的)而且可以是未取代的或取代的(优选未取代的)烃基,这些烃基具有1-8、优选l-6、特别优选1-4个碳原子(最优选甲基或乙基);基团R′之间是相同的或不同的而且可以是未取代的或取代的烃基,这些烃基具有1-20个碳原子;x为1,2或3。
上面结构式中R′基团的例子是烷基、链烯基、芳基、烷基芳基、芳基烷基、芳基链烯基和链烯基芳基(每种情况下优选具有1-12个,特别是1-8个碳原子的基团,并且包括环状基团),这些基团可以嵌入氧原子、硫原子、氮原子或NR″基团(R″是氢或C1-4的烷基)并且可以具有一个或多个取代基。这些取代基选自卤素和未取代的或取代的氨基、酰胺基、羧基、巯基、异氰酸根、羟基、烷氧基、烷氧基羰基、丙烯酰氧基、甲基丙烯酰氧基或环氧基。
在上述通式(Ⅰ)的烷氧基硅烷中,至少有一种是优选的,其中的至少一个R′基具有可进行加聚(包括聚加成反应)或缩聚反应的基团。
这种可进行加聚或缩聚反应的基团优选包含环氧基或(最好是活化的)碳碳多重键(特别是双键),(甲基)丙烯酸基是最后提到的基团的特别优选的例子。
因此,在用于本发明的通式(Ⅰ)的有机改性烷氧基硅烷中,特别优选这样的有机改性烷氧基硅烷,其中x是2或3并优选3,而且一个基团(唯一的基团)R′是ω-缩水甘油氧基-C2-6烷基或ω-(甲基)丙烯酰氧基-C2-6烷基。
这种硅烷的特例是3-缩水甘油氧基丙基三(甲)乙氧基硅烷、3,4-环氧丁基三甲氧基硅烷、2-(3,4-环氧环己基)乙基三甲氧基硅烷、以及3-(甲基)丙烯酰氧基丙基三(甲)乙氧基硅烷和2-(甲基)丙烯酰氧基乙基三(甲)乙氧基硅烷。其中x为1或2的适宜化合物的例子,还有3-缩水甘油氧基丙基二甲基(甲)乙氧基硅烷、3-缩水甘油氧基丙基甲基二(甲)乙氧基硅烷、3-(甲基)丙烯酰氧基丙基甲基二(甲)乙氧基硅烷和2-(甲基)丙烯酰氧基丙基甲基二(甲)乙氧基硅烷。
此外,可独立使用(如果需要,最好和含有上述可进行加聚或缩聚反应基团的烷氧基硅烷一起使用)的烷氧基硅烷的例子是四甲氧基硅烷、四乙氧基硅烷、四n-丙氧基硅烷、四n-丁氧基硅烷、环己基三甲氧基硅烷、环戊基三甲氧基硅烷、乙基三甲氧基硅烷、苯乙基三甲氧基硅烷、苯基三甲氧基硅烷、n-丙基三甲氧基硅烷、环己基甲基二甲氧基硅烷、二甲基二甲氧基硅烷、二异丙基二甲氧基硅烷、苯基甲基二甲氧基硅烷、苯乙基三乙氧基硅烷、苯基三乙氧基硅烷、苯基甲基二乙氧基硅烷和苯基二甲基乙氧基硅烷。
特别地,如果希望本发明的纳米模具和薄膜具有排斥污垢和水的特性和低的表面能,可以将硅烷与有机改性烷氧基硅烷一起使用,该硅烷具有与硅直接相连的氟化烷基(至少具有4个碳原子,并且最好具有至少3个氟原子),其中占据硅α位和β位的碳原子最好不带有氟原子。这种硅烷的例子有(十三氟-1,1,2,2-四氢辛基)甲基二乙氧基硅烷、(十三氟-1,1,2,2-四氢辛基)三乙氧基硅烷、(十七氟-1,1,2,2-四氢癸基)甲基二乙氧基硅烷和(十七氟-1,1,2,2-四氢癸基)三乙氧基硅烷。
当然,除上述硅烷(特别是有机改性硅烷)之外,那些具有可水解烷氧基基团的非硅烷类物质也可以用于本发明。这种非硅烷类的物质的例子是铝、钛、锆、钽、铌、锡、锌、钨、锗和硼的醇盐(优选具有C1-4烷氧基的醇盐)。这类化合物的特例是仲丁醇化铝、异丙醇钛盐、丙醇钛盐、丁醇钛盐、异丙醇锆盐、丙醇锆盐、丁醇锆盐、乙醇锆盐、乙醇钽盐、丁醇钽盐、乙醇铌盐、丁醇铌盐、特丁醇锡盐、乙醇钨(Ⅳ)盐、乙醇锗盐、异丙醇锗盐及二-叔丁氧基铝三乙氧基硅烷。
特别是当醇盐(如Al、Ti、Zr等的醇盐)相对比较活泼时,建议以它们的络合形式来使用,适宜的络合剂如不饱和羧酸及β-二羰基化合物,例如甲基丙烯酸、乙酰丙酮和乙酰乙酸乙酯。如果除了有机改性烷氧基硅烷之外,还使用含可水解烷氧基的物质,那么有机改性烷氧基硅烷与其它物质的摩尔比至少为2∶1,最好,特别是至少为5∶1,优选至少为10∶1。
在本发明的方法中,如果使用(最好是使用)含可进行加聚或缩聚反应基团的有机改性烷氧基硅烷,那么最好将引发剂混入相应的组合物,此引发剂与有机基团的摩尔比通常不超过0.15∶1。
例如,当使用通式(Ⅰ)的硅烷含有环氧基时,特别适宜的的引发剂包括咪唑、胺、酸酐及Lewis酸。当使用咪唑时,1-甲基咪唑是特别优选的。其它优选的咪唑引发剂是2-甲基咪唑和2-苯基咪唑。选自伯、仲、叔胺的引发剂有:乙二胺、二亚乙基三胺、三亚乙基四胺、1,6-二氨基己烷、1,6-二(二甲基氨基)己烷、四甲基乙二胺、N,N,N′,N″,N″-五甲基二亚乙基三胺、1,4-二氮杂环[2.2.2]辛烷、1,2-二氨基环己烷、2-氨甲基-3,3,5-三甲基环戊基胺、4,4′-二氨基环己基甲烷、1,3-双(氨甲基)环己烷、双(4-氨基-3-甲基环己基)甲烷、1,8-二氨基-P-甲烷、3-氨乙基-3,3,5-三甲基环己基胺(异佛尔酮二胺)、哌嗪、哌啶、乌洛托品、二(4-氨基苯基)甲烷和二(4-氨基苯基)砜。用作引发剂的胺还可用硅烷的官能化,这样的例子有:N-(2-氨基乙基)-3-氨基丙基三乙氧基硅烷、N-(2-氨基乙基)-3-氨基丙基三甲氧基硅烷、氨基丙基三甲氧基硅烷和氨基丙基三乙氧基硅烷。另外,也可以使用胺的三氟化硼加合物,例如,BF3-乙胺。进一步地,要导致有机交联,还可以借助于酸酐(最好与叔胺一起),例如,乙基双环[2.2.1]己烯-2,3-二甲酸酐、六氢化萘二甲酸酐、邻苯二甲酸酐、1,2-环己烷二甲酸酐以及[3-(三乙氧基甲硅烷基)丙基]琥珀酸酐。
此外,适合于目前情况下的环氧基基团交联的催化剂是(任意预水解的)铝、钛和锌的醇盐(如Al(OC2H4OC4H9)3)和有机羧酸(如丙酸)。
当使用上述通式(Ⅰ)的具有(甲基)丙烯酸基团的硅烷时,可将常规的热聚合催化剂或光聚合催化剂加到组合物中。优选使用的热聚合催化剂的例子是偶氮二异丁腈、二酰基过氧化物(如过氧化二苯甲酰和过氧化二月桂酰)、过氧化碳酸酯、过氧化烷基酯、过氧缩酮、烷基或芳基过氧化物、酮过氧化物和过氧化氢。
当然也可以将纯的有机组分混入组合物,该有机组分可与通式(Ⅰ)的硅烷上的活性基团发生反应,因此在固化过程中可以导致进一步的交联。例如,当使用含有(甲基)丙烯酸基团的硅烷时,有用的交联剂的特例是双酚A二丙烯酸酯、双酚A双甲基丙烯酸酯、三羟甲基丙烷三丙烯酸酯、三羟甲基丙烷三甲基丙烯酸酯、新戊二醇二甲基丙烯酸酯、新戊二醇二丙烯酸酯、二乙二醇二丙烯酸酯、二乙二醇二甲基丙烯酸酯、三乙二醇二丙烯酸酯、三乙二醇二甲基丙烯酸酯、四乙二醇二丙烯酸酯、四乙二醇二甲基丙烯酸酯、聚乙二醇二丙烯酸酯、聚乙二醇二甲基丙烯酸酯、2,2,3,3-四氟代-1,4-丁二醇二丙烯酸酯和二甲基丙烯酸酯、1,1,5,5-四氢全氟代戊基-1,5-二丙烯酸酯和二甲基丙烯酸酯、六氟代双酚A二丙烯酸酯和二甲基丙烯酸酯、八氟代-1,6-己二醇二丙烯酸酯和二甲基丙烯酸酯、1,3-二(3-甲基丙烯酰氧基丙基)四(三甲基甲硅氧基)二硅氧烷、1,3-二(3-丙烯酰氧基丙基)四(三-甲基甲硅氧基)二硅氧烷、1,3-二(3-甲基丙烯酰氧基丙基)四甲基二硅氧烷和1,3-二(3-丙烯酰氧基丙基)四甲基二硅氧烷。
如果期望纳米模具和薄膜具有亲水特性,例如,还可以将导致这种亲水特性的组分引入本发明的组合物中。为此,可以使用能够与无机基材形成共价键的组分(如具有自由羟基的组分,例如(甲基)丙烯酸2-羟乙酯),或者使用可在基材中自由移动的亲水组分(如表面活性剂),或者将二者组合使用。
为了使含可水解烷氧基的物质和/或相应的预缩合物(进一步)水解,本发明所使用的条件最好包含:每摩尔的可水解烷氧基至少存在0.5摩尔的水。由于溶胶中的水,通常这样的水量已经存在。如果情况不是这样,那么就应独立地补加相应数量的水。
如果存在烷氧基水解(和缩合)的催化剂,将是更优选的。酸性催化剂,例如含水(无机)酸如HCl,是此目的的优选催化剂。
所用原料(溶胶和含可水解烷氧基的物质)的比例最好这样选择,使得最终的模具或最终的薄膜(固化后)中的固含量(源自溶胶),分别占模具或薄膜重量的1-50%,特别是5-30%。
在导致含可水解烷氧基物质水解的条件下,将水溶胶和/或醇溶胶与含可水解烷氧基的物质接触的方法,对熟练的技术人员而言是熟悉的,并且此方法将在下面的实施例中得到进一步的阐明。伴随溶剂(醇)从组合物(通常意味着有10-80%,特别是20-50%的初始的可水解烷氧基已进行了缩合反应)中除去,可以证实这样做是有益的,即为特定的目的,通过加水将产物组合物调整到合适的粘度。此组合物的粘度,尤其是用作涂覆目的,最好低于5000mPas,特别是低于3000mPas。
为了借助于本发明的组合物制备纳米模具和带有纳米薄膜的基材,可将这种组合物引入模具或者施用于基材,然后-如果需要,在室温或稍高的温度下预先干燥之后,尤其是制备薄膜时-进行热固化(另外,如果需要,可进行光化学固化)。制备薄膜时,可以使用所有的常规涂覆技术,如浸涂、流涂、辊涂、喷涂、刮涂、旋涂或丝网印刷。
固化温度的范围通常为90-300℃,特别是110-200℃,尤其是制备薄膜时,还取决于要涂覆的基材的温度稳定性。
象开始时提到的那样,适于本发明的组合物涂覆的基材种类非常广,对于这些基材甚至不需要表面处理,多数情况下展现出良好的粘附性和极高的抗划伤性。特别优选的用作薄膜制备的基材是玻璃、透明或不透明塑料和金属。合适的塑料有聚碳酸酯、聚(甲基)丙烯酸酯、聚苯乙烯、聚氯乙烯、聚对苯二甲酸乙二醇酯、聚丙烯和聚乙烯,优选的金属基材是铝。
因此,根据本发明所获得的组合物适合于大量的应用。这些应用的例子如下:
增强抗划伤和抗磨损的涂覆:
-家用物品和运输工具的面涂层
-透明和不透明的聚合物组分
-金属基材
-陶瓷和玻璃基材
提高贵金属和非贵金属抗磨损和抗腐蚀的涂覆:
-Mg:发动机组、眼睛架、体育设施、轮缘、传动箱
-Al:运输工具的车体、轮缘、饰面元件、家具、热交换器
-钢:生产部件的压模、卫生设备
-Zn:屋顶构造、轻武器、安全气囊加速计滑块
-Cu:门用附件、热交换器、脸盆
提高清洁行为的涂覆:
有关这类应用的例子,参见DE-A-19544763。
提高脱模和降低粘附性的涂覆:
-金属和聚合物传送带
-聚合反应的滚筒
-生产聚苯乙烯部件的压模
-面涂层和饰面的抗乱涂写涂覆
抗冷凝效应的涂覆:
-运输工具的玻璃制品
-眼睛片
-镜子(如浴室镜、汽车的倒视镜和化装镜)
-光学部件(如光谱仪的镜子和激光的棱镜)
-包装组件(如气象仪器的外壳)
抗反射特性的涂覆:
-显示元件的聚合物或玻璃屏(如汽车仪表板、显示窗口的玻璃)
与食品相关的涂覆:
-扩散障碍层(防止如气体、乙醛、铅离子或碱金属离子、气味和香味的扩散)
中空玻璃制品的涂覆:
-饮料瓶的涂覆,以增加破裂压力
-通过涂覆使无色玻璃着色
光学模具和自持薄膜的生产:
-纳米级柔性焦距透镜组
-抗划伤和抗磨损包装薄膜
实施例起对本发明作进一步解释的作用。在所有的实施例中,由水解所形成的溶剂(乙醇)至少近95%被除去。
实施例1
在27.8g(0.1mol)的(3-缩水甘油氧基丙基)三乙氧基硅烷(GLYEO)中,混入27.8g的二氧化硅溶胶(重量浓度30%的SiO2水溶液,Bayer出品的Levasil200S)。然后将所得到的混合物在室温下搅拌5小时。其后,再通过蒸馏(旋转蒸发器,最高浴温40℃),将水解所形成的乙醇除去。在剩余物中混入1.11g(0.0005mol)的N-(2-氨基乙基)-3-氨基丙基三甲氧基硅烷(DIAMO),并在室温下搅拌1小时。
用所得的产物涂覆聚碳酸酯薄板、铝薄板和CR-39透镜。已通过电晕放电对聚碳酸酯薄板进行了预处理。已涂覆的聚碳酸酯薄板和铝薄板在室温存放30分钟,然后在130℃下固化4小时。CR-39透镜在室温存放30分钟,然后在90℃下固化4小时。
实施例2
重复实施例1,只是用3.05g(0.001mol)的[3-(三乙氧基甲硅烷基)丙基]琥珀酸酐(GF20)代替DIAMO。通过泰伯(Taber)磨耗试验(轮子材料为CS10F,1000转,轮子载荷500g),对涂覆了此组合物的聚碳酸酯薄板进行抗磨损研究,结果散射光损失7%。
实施例3
重复实施例1,只是用勃姆石悬浮液(2.78g的DisperalP3溶于25g蒸馏水中)代替二氧化硅溶胶。
实施例4
重复实施例3,只是3.78g(0.01mol)的Al(OEtOBu)3代替DIAMO作催化剂。
实施例5
在27.8g(0.1mol)的GLYEO中,混入27.8g如实施例1所描述的二氧化硅溶胶。然后将所得到的混合物在室温下搅拌5小时,再按实施例1所描述的那样,将水解所形成的乙醇除去。在剩余物中混入2.84g(0.01mol)的TiO2溶胶,并在室温下搅拌1小时。
TiO2溶胶是这样制备的,即将28.42g(0.1mol)的原钛酸四异丙酯(Ti(OiPr)4)溶解于60ml的异丙醇中,并按1∶1的摩尔比将浓盐酸加到溶液中。在室温下搅拌2小时之后,通过旋转蒸发器除去挥发性成分,并将剩余物吸收于70ml的水中。
实施例6
139.0g(0.5mol)的GLYEO与62.4g(0.3mol)的四乙氧基硅烷(TEOS)混合。在反应混合物中混入HCl-酸化的勃姆石悬浮液(12.82g的纳米级勃姆石粉末溶于128.20g的0.1N HCl溶液),并在室温下搅拌5小时。再按实施例1所描述的那样,通过蒸馏将水解所形成的乙醇除去。然后,向混合物中加入3.78g(0.01mol)的Al(OEtOBu)3,随后在室温下搅拌1小时。
用这样制备的组合物,涂覆经电晕放电预处理过的聚碳酸酯板和等离子体预处理过的CR-39透镜,并分别在130℃和90℃热固化1小时。
实施例7
在29.0g(0.1mol)的3-甲基丙烯酰氧基丙基三乙氧基硅烷中,混入29.0g如实施例1所描述的二氧化硅溶胶,并在室温下搅拌16小时。然后在所得的混合物中混入13.0g(0.1mol)的甲基丙烯酸2-羟乙酯(作为亲水组分),并在室温下搅拌30分钟。紧接着再按实施例1所描述的那样,通过蒸馏将水解所形成的乙醇从反应混合物中除去。向浓缩的反应混合物中加入0.48g的过氧化二苯甲酰(按存在的双键计为1mol%)。
将这样制备的组合物,施用于经电晕放电预处理过的聚甲基丙烯酸甲酯薄板,并分别在95℃热固化4小时。
实施例8
在55.6g的3-缩水甘油氧基丙基三乙氧基硅烷中,混入0.51g的十三氟-1,1,2,2-四氢辛基-1-三乙氧基硅烷并搅拌。向产物混合物混入10.85g的0.1NHCl(与烷氧基硅烷水解所需要的化学计量量的水相当)。室温下搅拌24小时之后,加入如实施例1所描述的二氧化硅溶胶55.6g,并将混合物在室温下搅拌4小时。通过旋转蒸发器,按实施例1所描述的那样,将水解所形成的醇除去(除去量为26.4g)。然后,将2.22g的DIAMO加到混合物中,并在室温下再搅拌混合物1小时。
实施例9
将278.42g的GLYEO和10g的反应产物(3-异氰酸根合丙基三乙氧基硅烷与聚乙二醇600的反应产物),与54g的0.1N HCl共水解,并在室温下搅拌5小时。用旋转蒸发器(浴温25℃,30-40mbar)除去预水解所形成的乙醇。然后,搅拌下将926g如实施例1所描述的二氧化硅溶胶加到此混合物中,之后将混合物在室温下搅拌16小时。其后,将11.12g作为引发剂的DIAMO加到混合物中,并在室温下再搅拌1小时。然后在剧烈搅拌下,加入20g聚硅氧烷基的非离子表面活性剂。
用产物组合物涂覆浮法玻璃基材,并在130℃的干燥烘箱中固化4小时。
实施例10
重复实施例1,只是用1.32g(0.005mol)的三甲氧基甲硅烷基丙基二亚乙基三胺(TRIAMO)代替DIAMO。
实施例11
重复实施例1,只是用0.74g(0.01mol)的丙酸作为引发剂代替DIAMO。
实施例12
重复实施例1,只是用3.87g(0.01mol)的Al(OEtOBu)3作为引发剂代替DIAMO。
实施例13
重复实施例1,只是用0.41g(0.005mol)的1-甲基咪唑作为引发剂代替DIAMO。
实施例14
重复实施例1,只是用5.27g(0.01mol)的混合物代替DIAMO,此混合物是通过用GF20A按1∶1的摩尔比在冰冷却下纯化3-氨基丙基三乙氧基硅烷(AMEO)而得到的。
实施例15
重复实施例6,只是用95.5g如实施例1所描述的二氧化硅溶胶代替HCl-酸化的勃姆石悬浮液,并增加5倍量的催化剂。
用产物组合物,涂覆经电晕放电预处理过的聚碳酸酯板和等离子体预处理过的CR-39透镜,并分别在130℃和90℃热固化1小时。
实施例16
在27.8g(0.1mol)的GLYEO中,混入13.5g 0.1N HCl,并在室温下搅拌2小时。将27.8g的有机溶胶(30%重量的SiO2溶于异丙醇,Bayer PPL6454-6456)加到此预水解物中,并将所得到的混合物在室温下搅拌5小时。然后,通过蒸馏将水解所形成的乙醇和异丙醇溶剂除去。在剩余物中混入18.9g的H2O(pH3.2)。其后,在剧烈搅拌下加入1.11g(0.0005mol)的DIAMO,并将混合物在室温下搅拌1小时。
用产物组合物涂覆聚碳酸酯薄板、铝薄板和CR-39透镜。已通过电晕放电对聚碳酸酯薄板进行了预处理。已涂覆的聚碳酸酯薄板和铝薄板在室温存放30分钟,然后在130℃下固化4小时。CR-39透镜在室温存放30分钟,然后在90℃下固化4小时。
实施例17
在139.0g(0.5mol)的GLYEO中,混入62.4g(0.3mol)的TEOS,并按化学计量量混入0.1N的盐酸。将反应混合物在室温下搅拌16小时。然后通过蒸馏将水解和缩合所形成的乙醇除去。然后,向浓缩的反应混合物中混入HCl-酸化的勃姆石悬浮液(12.82g的纳米级勃姆石粉末溶于128.8g的0.1NHCl溶液),并在室温下搅拌3小时。然后,向混合物中滴加3.78g(0.01mol)的Al(OEtOBu)3。将如此制备的涂覆材料在室温下搅拌大致4小时。
涂覆经电晕放电预处理过的聚碳酸酯薄板和等离子体预处理过的CR-39透镜,并分别在130℃和90℃热固化1小时。
实施例18
在139.0g(0.5mol)的GLYEO中,混入62.4g(0.3mol)的TEOS,并按化学计量量混入0.1N的盐酸。将反应混合物在室温下搅拌16小时。然后通过蒸馏将水解和缩合所形成的乙醇除去。然后,向浓缩的反应混合物中混入30%重量的已酸化的二氧化硅溶胶溶液(参见实施例1),并在室温下搅拌3小时。然后,向混合物中滴加18.9g(0.05mol)的Al(OEtOBu)3。将如此制备的涂覆材料在室温下搅拌大致4小时。
涂覆经电晕放电预处理过的聚碳酸酯薄板和等离子体预处理过的CR-39透镜,并分别在130℃和90℃热固化1小时。
实施例19
在27.8g(0.1mol)的GLYEO中,混入0.51g的氟代硅烷(参见实施例8;相对于GLYEO为1mol%)并搅拌混合物。向混合物中混入5.46g的0.1NHCl,与水解所需的化学计量量的水相当。然后将混合物在室温下搅拌24小时。然后通过旋转蒸发器将水解和缩合所形成的醇除去。向剩余物中混入3.87g(0.01mol)的Al(OEtOBu)3和27.8g的已酸化的二氧化硅溶胶(参见实施例1),并在室温下搅拌3小时。
实施例20
在27.8g(0.1mol)的GLYEO中,混入0.225g的氟代硅烷(参见实施例8;相对于GLYEO为0.5mol%)并搅拌混合物。向混合物中混入5.43g的0.1NHCl,与水解所需的化学计量量的水相当。然后将混合物在室温下搅拌24小时,并通过旋转蒸发器将水解和缩合所形成的醇除去。除去量(约13g)相当于约95%。将剩余物分散于勃姆石悬浮液(2.78g的DispersalP3溶于0.1N的盐酸溶液),并混入1.89g(0.005mol)的Al(OEtOBu)3,并在室温下搅拌1小时。
Claims (19)
1.制备组合物的方法,该组合物是用来制备纳米模具和纳米薄膜,包括在导致物质(进一步)水解的条件下,让选自硅和周期表中的主族及过渡族金属元素化合物的水溶胶和/或醇溶胶,与具有可水解的烷氧基、至少包括一种有机改性烷氧基硅烷或由它而得到的预缩合物的物质接触,然后将所产生的醇或原来就存在的任何醇除去,其特征在于,是按这样的数量脱醇,使组合物中剩余的醇含量不超过20%(重量)。
2.权利要求1的方法,其中除了初始就已经存在的任何醇的总量之外,脱醇的数量相当于初始存在的烷氧基全部水解的理论产醇量的至少30%(重量),特别是至少50%(重量)。
3.权利要求1和2之一的方法,其中脱醇之后,向组合物中加水以控制适宜的粘度。
4.权利要求1-3之一的方法,其中使用了水溶胶。
5.权利要求1-4之一的方法,其中构成该溶胶的化合物由至少一种元素衍生而来,该元素选自硅和周期表中的第三、第四主族以及第三至第五过渡族金属,优选由Si、Al、Sn、Ti或Zr衍生而来的化合物。
6.权利要求1-5之一的方法,其中构成该溶胶的化合物包含至少一种氧化物(水合物)、硫化物、硒化物或磷酸盐,优选氧化物(水合物)。
7.权利要求1-6之一的方法,其中该溶胶是SiO2、Al2O3、AlOOH、TiO2和/或ZrO2溶胶。
8.权利要求1-7之一的方法,其中该有机改性烷氧基硅烷包含至少一种通式(Ⅰ)的化合物:
R′4-xSi(OR)x (Ⅰ)这里基团R是具有1-8个碳原子的未取代的或取代的烃基,基团R′互相之间是相同的或不同的,并且每个R′是具有1-20个碳原子的未取代的或取代的烃基;x为1,2或3。
9.权利要求8的方法,其中的基团R是C1-4的烷基,优选甲基和乙基;x是2或3,优选3;基团R′,或至少一个R′基团,具有可进行加聚或缩聚反应的基团。
10.权利要求9的方法,其中该可进行加聚或缩聚反应的基团是环氧基或优选活化了的碳-碳多重键,特别优选(甲基)丙烯酸基团。
11.权利要求8-10之一的方法,其中的基团R′,或至少一个R′基团,是ω-缩水甘油氧基-C2-6烷基或ω-(甲基)丙烯酰氧基-C2-6烷基。
12.权利要求9-11之一的方法,其中的组合物中加有加聚或缩聚反应的催化剂。
13.权利要求1-12之一的方法,其中导致具有可水解基团的物质(进一步)水解的条件包含:(a)每个可水解的烷氧基至少存在0.5mol的H2O,和(b)优选存在水解反应的酸性催化剂。
14.权利要求1-13之一的方法,其中该溶胶按这样的数量加入,使得最终模具或最终薄膜中的溶胶固含量分别占模具或薄膜重量的1-50%,并优选5-30%。
15.由权利要求1-14之一的方法获得的制备纳米模具和薄膜的组合物。
16.制备纳米模具和带有纳米薄膜的基材的方法,其中将根据权利要求1-14之一的方法制备的组合物
(a)引入模具;或
(b)施用于基材;和随后进行热固化及另外的光化学固化(如果需要)。
17.权利要求16的方法,其中该基材为玻璃、塑料或金属。
18.由权利要求16和17之一的方法获得的纳米模具和带有纳米薄膜的基材。
19.权利要求18的纳米模具和带有纳米薄膜的基材,用于光学用途。