DE10136456A1

DE10136456A1 - Antimicrobial wallpaper comprises aminoalcohol(s), e.g. aminomethanol, in the form of a polymer-containing coating or incorporated into the paper

Info

Publication number: DE10136456A1
Application number: DE2001136456
Authority: DE
Inventors: Peter Ottersbach; Beate Kossmann
Original assignee: Creavis Gesellschaft fuer Technologie und Innovation mbH
Current assignee: Creavis Gesellschaft fuer Technologie und Innovation mbH
Priority date: 2001-07-26
Filing date: 2001-07-26
Publication date: 2003-02-20

Abstract

Wallpaper comprises 0.01-40 wt.% of aminoalcohol(s) (I). An Independent claim for production of antimicrobial wallpaper that comprises application of a coating containing (I) to paper substrate.

Description

Die Erfindung betrifft mikrobizide Tapeten, die Aminoalkohole enthalten. The invention relates to microbicidal wallpapers containing amino alcohols.

Besiedlungen und Ausbreitungen von Bakterien auf Oberflächen von Rohrleitungen, Behältern oder Verpackungen sind im hohen Maße unerwünscht. Es bilden sich häufig Schleimschichten, die Mikrobenpopulationen extrem ansteigen lassen, die Wasser-, Getränke- und Lebensmittelqualitäten nachhaltig beeinträchtigen und sogar zum Verderben der Ware sowie zur gesundheitlichen Schädigung der Verbraucher führen können. Colonization and spread of bacteria on surfaces of pipes, containers or packaging is highly undesirable. Mucus layers often form, make the microbe populations extremely high, the water, beverage and Permanently affect food quality and even spoil the goods as well can lead to health damage to consumers.

Aus allen Lebensbereichen, in denen Hygiene von Bedeutung ist, sind Bakterien fernzuhalten. Davon betroffen sind Textilien für den direkten Körperkontakt, insbesondere für den Intimbereich und für die Kranken- und Altenpflege. Außerdem sind Bakterien fernzuhalten von Möbel- und Geräteoberflächen in Pflegestationen, insbesondere im Bereich der Intensivpflege und der Kleinstkinder-Pflege, in Krankenhäusern, insbesondere in Räumen für medizinische Eingriffe und in Isolierstationen für kritische Infektionsfälle sowie in Toiletten. Bacteria must be kept away from all areas of life where hygiene is important. This affects textiles for direct body contact, especially for Intimate area and for nursing and elderly care. Bacteria should also be kept away from furniture and device surfaces in care stations, especially in the area of intensive care and Care of infants, in hospitals, especially in rooms for medical interventions and in isolation stations for critical infections and in toilets.

Daneben gibt es auch eine Reihe technischer Systeme, die durch mikrobiellen Bewuchs in ihrer Leistungsfähigkeit stark eingeschränkt oder aber sogar gänzlich unbrauchbar werden. Insbesondere Systeme zur Stofftrennung, wie z. B. Membranen oder Filter, werden durch mikrobielle Ablagerungen und Bewuchs stark beeinträchtigt. So verkürzt z. B. bei der Meerwasserentsalzung der Bewuchs der Systeme mit Meeresalgen die Laufzeiten oft beträchtlich. Bei anderen Systemen, wie z. B. der Tiefenfiltration, kann der Filterkuchen durch aufgewachsene Biofilme vorzeitig verstopfen. Dem versucht man bei der Querstromfiltration durch Einsatz einer definierten Strömung quer zur Filtrationsebene zu begegnen, was sich in der Praxis aber bisher als nicht ausreichend zur Verhinderung des Aufwachsens von Biofilmen gezeigt hat. There are also a number of technical systems that are characterized by microbial growth in their Performance severely limited or even completely unusable. In particular systems for material separation, such as. B. membranes or filters are through microbial deposits and growth are severely impaired. So shortened z. B. at the Desalination of the vegetation of the systems with seaweed often times considerably. In other systems, such as. B. the deep filtration, the filter cake through Clogged biofilms prematurely. This is tried in cross-flow filtration to counteract what is in by using a defined flow across the filtration level in practice, however, so far not sufficient to prevent the growth of biofilms showed.

Gegenwärtig werden Geräte, Oberflächen von Möbeln und Textilien gegen Bakterien im Bedarfsfall oder auch vorsorglich mit Chemikalien oder deren Lösungen sowie Mischungen behandelt, die als Desinfektionsmittel mehr oder weniger breit und massiv antimikrobiell wirken. Solche chemischen Mittel wirken unspezifisch, sind häufig selbst toxisch oder reizend oder bilden gesundheitlich bedenkliche Abbauprodukte. Häufig zeigen sich auch Unverträglichkeiten bei entsprechend sensibilisierten Personen. Devices, surfaces of furniture and textiles are currently used to fight bacteria in the If necessary or as a precaution with chemicals or their solutions and mixtures treated as a disinfectant more or less broad and massive antimicrobial Act. Such chemical agents have a non-specific effect and are often themselves toxic or irritating or form degradation products that are harmful to health. Often show up too Incompatibilities in appropriately sensitized people.

Eine aus gesundheitsprophylaktischer Sicht sehr wichtige Aufgabe stellt die Vermeidung von Mikroben-, insbesondere Schimmelpilzbefall, von Raumoberflächen, insbesondere Innenflächen von bewohnten Räumen dar. Als besonders kritisch erweisen sich in diesem Zusammenhang tapezierte Oberflächen, da diese das "Atmen" der Bausubstanz behindern, was einerseits zur verstärkten Kondensation von Luftfeuchtigkeit und andererseits zu einer verminderten Feuchtigkeitsabgabe und damit verbundenen Trocknung von feuchten Wänden beiträgt. Dies ist umso bedeutsamer, da gerade die deutsche Bevölkerung als die "tapezierfreudigste" der Welt gilt. So verklebt statisch betrachtet jeder Bundesbürger fast zwei Rollen pro Jahr, was insgesamt einer Gesamtmenge von ca. 140 Millionen Tapetenrollen entspricht. Allein zur Herstellung geschäumter Vinyltapeten werden, mit steigender Tendenz, hierzulande jährlich 25.000 Tonnen PVC-Paste eingesetzt. A very important task from a health prophylactic point of view is the avoidance of Microbial, in particular mold infestation, of room surfaces, in particular interior surfaces of inhabited rooms. Particularly critical in this context prove to be Wallpapered surfaces, as these hinder the "breathing" of the building structure, which on the one hand leads to increased condensation of humidity and on the other hand to a reduced Releases moisture and the associated drying of damp walls. This is all the more important since the German population in particular is the "most eager to paper" the World applies. From a static perspective, every citizen glues almost two roles a year, what corresponds to a total of approximately 140 million rolls of wallpaper. Alone for The production of foamed vinyl wallpaper is, with increasing tendency, annually in this country 25,000 tons of PVC paste used.

Diese beliebten Vinyltapeten werfen in Bezug auf den Feuchtigkeitsaustausch allerdings auch besondere Probleme auf. So erreicht die Wasserdampfdiffusionsfähigkeit, welche durch die DIN 52615 in Form einer equivalenten Luftschichtdicke klassifiziert wird, bei Papiertapeten Werte zwischen 5 bis 10 Zentimeter, bei PVC-Tapeten demgegenüber Werte von 200 bis 300 Zentimeter. Vinyltapeten zeigen demnach gegenüber Papiertapeten eine deutlich verminderte Atmungsfähigkeit. These popular vinyl wallpapers also throw in terms of moisture exchange special problems. So the water vapor diffusion ability achieved by the DIN 52615 is classified in the form of an equivalent air layer thickness for paper wallpapers Values between 5 and 10 centimeters, in contrast with PVC wallpapers values of 200 to 300 Centimeter. Vinyl wallpapers therefore show a significantly reduced rate compared to paper wallpapers Breathability.

Als Folge dieser verminderten Atmungsfähigkeit kondensiert Feuchtigkeit zwischen Wand und Tapete, was in einer verstärkten Schimmelpilzbildung resultiert. Desweiteren sind Vinyltapeten oft mit niedermolekularen Weichmachern versetzt, die ihrerseits von Mikroorganismen verstoffwechselt werden können und somit einen mikrobiellen Bewuchs zusätzlich stimulieren. Da der Bewuchs oft unterhalb der sichtbaren Oberfläche stattfindet, lassen sich kontaminierte Stellen optisch auch sehr schlecht bestimmen. Daher stellt man derartige Belastungen oft erst durch ihre gesundheitsschädlichen Auswirkungen in Form von Haut- und Atemwegserkrankungen bzw. allergischen Reaktionen auf betroffene Personen fest, die durch Schimmelpilzsporen in der Umgebungsluft induziert werden. Am häufigsten werden bei sporadisch stattfindenden Raumluftmessungen hierzulande die Schimmelpilzgattungen Aspergillus und Cladosporium nachgewiesen. As a result of this reduced breathability, moisture condenses between the wall and Wallpaper, which results in increased mold formation. Furthermore there are vinyl wallpapers often mixed with low molecular weight plasticizers, which in turn are from microorganisms can be metabolized and thus additionally stimulate microbial growth. Since the vegetation often takes place below the visible surface, contaminated ones can be Determine places optically very bad. That is why you often put such loads on due to their harmful effects in the form of skin and Respiratory illnesses or allergic reactions to affected people Mold spores can be induced in the ambient air. The most common are at Sporadic indoor air measurements in this country are the mold types Aspergillus and Cladosporium detected.

Um einen mikrobiellen Befall zu vermeiden bzw. zu unterdrücken, der auf die Anwesenheit von Feuchtigkeit und Nährstoffen aus Oberflächenmaterialien, wie z. B. den beschriebenen Weichmachern, angewiesen ist, bietet sich gerade bei Vinyltapeten eine Ausrüstung mit Bioziden an. Bis heute verwendet man dazu im Allgemeinen toxische Chemikalien, die in sogenannten "Antischimmelfarben" oder "Schimmelvernichtern" verwendet werden. Beispiele für derartig bedenkliche Stoffe sind Natriumhypochlorit, Formaldehyd oder auch Isothiazolinderivate. Alle diese Verbindungen gelten neben ihrer akuten Toxizität auch als allergieauslösend. Daneben werden diese Verbindungen relativ rasch verbraucht, so dass entweder die Schutzwirkung nach einer relativ kurzen Phase verpufft oder aber ein erneuter Einsatz dieser toxischen Substanzen vonnöten ist. In order to avoid or suppress a microbial infestation that indicates the presence of moisture and nutrients from surface materials such as B. the described Softeners, instructed, is particularly suitable for vinyl wallpapers Biocides. To date, toxic chemicals that are used in so-called "anti-mold paints" or "mold killers" can be used. Examples for substances of such concern are sodium hypochlorite, formaldehyde or Isothiazoline derivatives. In addition to their acute toxicity, all of these compounds are also considered to be allergenic. In addition, these connections are consumed relatively quickly, so that either the protective effect is lost after a relatively short phase or a renewed one Use of these toxic substances is necessary.

Als Alternative hierzu werden Substanzen gesucht, die über einen langen Zeitraum hinweg eine effiziente mikrobizide Wirkung zeigen, sich möglichst wenig bis gar nicht toxisch gegenüber höheren Organismen verhalten, nicht in die Raumluft abgegeben werden und die anwendungstechnischen Eigenschaften des zu imprägnierenden Materials nahezu unbeeinflußt lassen. As an alternative, substances are sought that have a long-term effect show efficient microbicidal effects, are as little as possible or not toxic to one another behave higher organisms, are not released into the room air and the application properties of the material to be impregnated almost unaffected to let.

Es wurde gefunden, dass sich Tapeten durch Aminoalkohole in ausreichender Weise mikrobizid ausrüsten lassen. It has been found that wallpaper by amino alcohols is sufficient Have a microbicide finish.

Gegenstand der vorliegenden Erfindung sind daher Tapeten, die 0,01-40 Gew.-% mindestens eines Aminoalkohols enthalten. The present invention therefore relates to wallpapers which are at least 0.01-40% by weight of an amino alcohol.

Dieser Gewichtsanteil bezieht sich auf die Tapete als solche, unabhängig davon, in welcher Schicht sich die Aminoalkohole befinden. This percentage by weight refers to the wallpaper as such, regardless of which Layer are the amino alcohols.

Die erfindungsgemäße Tapete kann in folgenden Ausführungsformen hergestellt werden:

- die Tapete besteht oder enthält ein Gemisch von Vinylpolymeren und mindestens eines Aminoalkohols,
- die Tapete besteht oder enthält ein Gemisch von Papierfasern und/oder Cellulose und/oder Textilfasern mit mindestens eines Aminoalkohols,
- die Tapete besteht oder enthält einen Papierträger mit einer Beschichtung, die mindestens einen Aminoalkohol enthält.

The wallpaper according to the invention can be produced in the following embodiments:

- the wallpaper consists or contains a mixture of vinyl polymers and at least one amino alcohol,
the wallpaper consists or contains a mixture of paper fibers and / or cellulose and / or textile fibers with at least one amino alcohol,
- The wallpaper consists or contains a paper backing with a coating that contains at least one amino alcohol.

Aminoalkohole in Zusammenhang mit antimikrobiellen Oberflächen sind z. B. aus DE 101 17 805 oder DE 101 06 230 bekannt. Amino alcohols in connection with antimicrobial surfaces are e.g. B. from DE 101 17 805 or DE 101 06 230 known.

Es war jedoch überraschend, das eine Verkeimung von großen Tapetenoberflächen bei im Vergleich großen Raumvolumina so effektiv durch die erfindungsgemäßen Tapeten verhindert werden konnte. It was surprising, however, that contamination of large wallpaper surfaces with im Comparison of large room volumes so effectively prevented by the wallpaper according to the invention could be.

Optional können die Aminoalkohole einem oder mehreren Polymeren zugemischt werden. Optionally, the amino alcohols can be mixed into one or more polymers.

Weitere Gegenstände der vorliegenden Erfindung sind Verfahren zur Herstellung von antimikrobiellen Tapeten. The present invention further relates to processes for the production of antimicrobial wallpaper.

Hierzu sind verschiedene Varianten möglich:

- Ein Papierträger wird mit einem Gemisch aus 0,01-40 Gew.-% mindestens eines Aminoalkohols enthaltend Polymer bzw. Polymerblend beschichtet.
- Es werden Fasern wie Textil-, Baumwoll-, Jute-, Seiden-, Viskose- oder Polymerfasern, die 0,01-40 Gew.-% mindestens eines Aminoalkohols enthalten, auf einem Papierträger befestigt.
- Es werden einem Gemisch aus Papier und/oder Zellstoff und/oder Textilien und/oder Cellulose und/oder Holzpartikeln und/oder Raufasern 0,01-40 Gew.-% mindestens eines Aminoalkohols zugegeben und dieses Gemisch wird zu einem Papierträger (Tapetenbahn), verarbeitet
- Es wird ein Gemisch aus Textil-, Baumwoll-, Jute-, Seiden-, Viskose- oder Polymerfasern auf einen Papierträger, der 0,01-40 Gew.-% mindestens eines Aminoalkohols enthält, befestigt.
- Ein Papierträger wird mit einer Beschichtung, die durch thermische Gelierung eines Plastisols enthaltend 0,01-40 Gew.-% mindestens eines Aminoalkohols, und bevorzugt E-PVC, ausgestattet.

Different variants are possible:

- A paper support is coated with a mixture of 0.01-40% by weight of at least one amino alcohol containing polymer or polymer blend.
- Fibers such as textile, cotton, jute, silk, viscose or polymer fibers containing 0.01-40% by weight of at least one amino alcohol are attached to a paper support.
- A mixture of paper and / or cellulose and / or textiles and / or cellulose and / or wood particles and / or woodchip fibers 0.01-40% by weight of at least one amino alcohol is added and this mixture is made into a paper carrier (wallpaper web) , processed
- A mixture of textile, cotton, jute, silk, viscose or polymer fibers is attached to a paper support containing 0.01-40 wt .-% of at least one amino alcohol.
- A paper carrier is provided with a coating which is obtained by thermal gelation of a plastisol containing 0.01-40% by weight of at least one amino alcohol, and preferably E-PVC.

Tapeten, insbesondere Vinyltapeten, lassen sich so mikrobizid ausrüsten, ohne die beschriebenen Nachteile des Standes der Technik zu beinhalten. Wallpaper, especially vinyl wallpaper, can be treated microbicide without the to include described disadvantages of the prior art.

Die so hergestellten Tapeten lassen sich prinzipiell zu allen Produkten weiterverarbeiteben, die auch bisher auf unmodifizierten Tapeten basieren. Dies gilt insbesondere für das Bedrucken bzw. Prägen der Tapeten, soweit dieses nicht schon im primären Herstellungsprozeß erfolgt. In principle, the wallpapers produced in this way can be further processed into all products that also previously based on unmodified wallpaper. This applies in particular to printing or embossing the wallpaper, unless this is already done in the primary manufacturing process.

Zur Herstellung der Tapeten können die allgemein bekannten Herstellungs- und Verarbeitungsverfahren Verwendung finden, wie sie in der einschlägigen Literatur, wie z. B. im Kunststoff-Handbuch Polyvinylchlorid, Band 2/2, 1986, S. 1077 bis 1128, näher beschrieben werden. The well-known manufacturing and Processing methods are used as they are in the relevant literature, such as. B. in Kunststoff-Handbuch Polyvinylchlorid, Volume 2/2, 1986, pp. 1077 to 1128, described in more detail become.

Durch die beschriebenen Vorgehensweisen erhält man antimikrobiell ausgerüstete Tapeten, die sowohl die erforderlichen mechanischen und Verarbeitungseigenschaften für die gestellten Aufgaben als auch die biochemische Hemmwirkung für das Mikrobenwachstum in nahezu idealer Weise miteinander verbinden. Da die Aminoalkohole in der Matrix der Tapeten fixiert sind und demzufolge keine niedermolekularen Bestandteile in die Umwelt und damit Raumluft freigesetzt werden, können solche Systeme auch in sensiblen Bereichen, wie z. B. der Auskleidung von Allergiker- und Schlafräumen, Verwendung finden, ohne dass mit einem toxikologisch bedenklichen Übertritt von Bioziden aus dem Produkt zu rechnen ist. Through the described procedures you get antimicrobial wallpaper, the both the required mechanical and processing properties for the posed Tasks as well as the biochemical inhibitory effect on microbial growth in almost ideally connect with each other. Because the amino alcohols are fixed in the matrix of the wallpaper are and therefore no low-molecular components in the environment and thus indoor air released, such systems can also be used in sensitive areas such as B. the Lining of allergy sufferers and bedrooms, find use without using one toxicologically questionable transfer of biocides from the product is to be expected.

Als Aminoalkohole kommen dabei prinzipiell alle aminofunktionalisierten Derivate von Alkoholen in Frage, insbesondere aber solche der folgenden Formel I

mit
R1 = verzweigter oder unverzweigter aliphatischer oder aromatischer Kohlenwasserstoffrest mit 1 bis 15 Kohlenstoffatomen.
R2 = H, verzweigter oder unverzweigter aliphatischer oder aromatischer Kohlenwasserstoffrest mit 1 bis 15 Kohlenstoffatomen.
R3 = H, verzweigter oder unverzweigter aliphatischer oder aromatischer Kohlenwasserstoffrest mit 1 bis 15 Kohlenstoffatomen. In principle, all amino-functionalized derivatives of alcohols are suitable as amino alcohols, but in particular those of the following formula I

With
R1 = branched or unbranched aliphatic or aromatic hydrocarbon radical with 1 to 15 carbon atoms.
R2 = H, branched or unbranched aliphatic or aromatic hydrocarbon radical with 1 to 15 carbon atoms.
R3 = H, branched or unbranched aliphatic or aromatic hydrocarbon radical with 1 to 15 carbon atoms.

Bevorzugt werden als Alkohole der Formel (I) tert.-Butylaminoethanol, tert.-Butylaminomethanol, tert.-Butylaminopropanol, 2-Butylaminoethanol, 2-Butylaminomethanol, 2- Butylaminopropanol, 2-Diethylaminoethanol, 2-Diethylaminomethanol, 2-Diethylaminopropanol, 2-Dimethylaminoethanol, 2-Dimethylaminomethanol, 2-Dimethylaminopropanol, Aminomethanol, Aminoethanol, Aminopropanol und/oder Aminobutanol eingesetzt. Preferred alcohols of the formula (I) are tert-butylaminoethanol, tert-butylaminomethanol, tert-butylaminopropanol, 2-butylaminoethanol, 2-butylaminomethanol, 2- Butylaminopropanol, 2-diethylaminoethanol, 2-diethylaminomethanol, 2-diethylaminopropanol, 2-dimethylaminoethanol, 2-dimethylaminomethanol, 2-dimethylaminopropanol, Aminomethanol, aminoethanol, aminopropanol and / or aminobutanol are used.

Das Verfahren der Erfindung gestaltet sich z. B. derart, dass einer Formulierung zur Herstellung einer Vinyltapete ein Aminoalkohol zugegeben wird. Im Anschluß daran findet während des Gelierprozesses vermutlich eine, zumindest partielle, Umsetzung des Aminoalkohols mit den anderen Bestandteilen der Formulierung statt. The method of the invention is such. B. such that a formulation for Making a vinyl wallpaper an amino alcohol is added. Following it takes place during the gelling process presumably an, at least partial, implementation of the Amino alcohol with the other ingredients of the formulation instead.

Es wird vermutet, dass der Aminoalkohol im Verlauf der Reaktion entweder in das entstehende polymere Netzwerk eingebaut oder aber bei Anwesenheit geeigneter Reaktionspartner über seine Hydroxy- oder Aminofunktion an das polymere Geflecht der enstehenden Vinyltapete fixiert wird. Als Kopplungsreaktionen kommen dabei prinzipiell alle Reaktionstypen der organischen Chemie in Betracht, welche mit Hydroxy- oder Aminogruppen unter Ausbildung chemischer Verbindungen reagieren, z. B. Veresterung oder Veretherung. Daneben spielen vermutlich auch rein physisch bedingte Kopplungsmechanismen, wie z. B. die Physisorption, eine entscheidende Rolle. It is believed that during the course of the reaction, the amino alcohol either enters the resulting one polymer network built in or in the presence of suitable reactants its hydroxy or amino function on the polymeric mesh of the vinyl wallpaper is fixed. In principle, all reaction types of the come as coupling reactions organic chemistry into consideration, which with hydroxy or amino groups under formation chemical compounds react, e.g. B. esterification or etherification. Play next to it probably also purely physical coupling mechanisms, such as B. physisorption, a crucial role.

Der Anteil der Aminoalkohole in den Tapeten kann 0,01 bis 40 Gew.-%, bevorzugt 0,1 bis 20, besonders bevorzugt 0,1 bis 10 Gew.-% betragen. The proportion of amino alcohols in the wallpaper can be 0.01 to 40% by weight, preferably 0.1 to 20 particularly preferably 0.1 to 10 wt .-%.

Als Polymer bzw. Polymerblend können PVC, Polyurethan, Polymethylmethacrylat, Polyethylen, Polypropylen eingesetzt werden. PVC, polyurethane, polymethyl methacrylate, Polyethylene, polypropylene can be used.

Die zur Beschichtung eingesetzten Plastisole enthalten neben dem Polymer - in der Regel E- PVC - z. B. Lösungsmittel, wie Kohlenwasserstoffe, Paraffine, Isopropanol oder Wasser, Stabilisatoren, Weichmacher (DINP, DOP, DINCH), Pigmente und ggf. Treibmittel wie Azodicarbonsäureamid. The plastisols used for coating contain not only the polymer - usually E- PVC - e.g. B. solvents such as hydrocarbons, paraffins, isopropanol or water, Stabilizers, plasticizers (DINP, DOP, DINCH), pigments and possibly blowing agents such as Azodicarbonamide.

Diese Plastisole können auf die gewünschten Träger (Papier, Textilien o. ä.) aufgetragen und durch Temperaturen von 100-200°C geliert werden. Der Einsatz von Treibmitteln ermöglicht die Herstellung von strukturierten Oberflächen. These plastisols can be applied to the desired carrier (paper, textiles or similar) and can be gelled by temperatures of 100-200 ° C. The use of blowing agents enables the production of structured surfaces.

Als Substrate können im Prinzip alle zur Herstellung von Tapeten verwendeten Makromoleküle Verwendung finden, insbesondere PVC und Papier. Dies gilt ebenfalls für auf diesen Substraten aufbauende Tapetensystemen, wie z. B. Rauhfaser-, Textil- und Naturfasertapeten. In principle, all can be used as substrates for the production of wallpapers Macromolecules are used, especially PVC and paper. This also applies to these substrates building wallpaper systems, such as. B. woodchip, textile and Natural fiber wallpaper.

Beispielhaft wird im Folgenden die Herstellung von erfindungsgemäßen Textil- und Rauhfasertapeten beschrieben: The following is an example of the production of textile and Woodchip wallpaper described:

textile wall coverings

Bei den Textiltapeten werden textile Materialien, wie z. B. die Naturfasern Baumwolle, Jute, Seide, Leinen, oder Kunstfasern wie Viskose, auf Papierträger aufgebracht. Im Allgemeinen geschieht die Aufbringung durch ein Aufkleben der Fasern bzw Fäden auf eine ein- oder mehrlagige Papierschicht. Bisweilen sind diese Tapeten zusätzlich noch bedruckt. Bei Velourtapeten, die ebenfalls zur Gruppe der Textiltapeten gehören, wird ein Kleberbett auf dem Papierträger mit kurzen Seiden- oder Kunstfasern elektrostatisch beflockt, wodurch die Flächen einen insgesamt samtigen Schimmer erhalten. In the textile wallpapers, textile materials such as. B. the natural fibers cotton, jute, Silk, linen, or synthetic fibers such as viscose, applied to paper backing. In general the application is done by gluing the fibers or threads onto one or multi-layer paper layer. Sometimes these wallpapers are also printed. at Velor wallpapers, which also belong to the group of textile wallpapers, will have an adhesive bed on them the paper carrier is electrostatically flocked with short silk or synthetic fibers, which makes the Surfaces get an overall velvety shimmer.

Gerade Naturtextilien sind in der Lage, in ihren Fasern Wasserdampf aus dem Raum aufzunehmen und wieder abzugeben und sorgen so für ein gesundes, angenehmes Raumklima. Allerdings birgt dieses Wasserdampfaufnahmevermögen auch ein Risiko zur Verkeimung, da die Fasern große Oberflächen besitzen, die von Mikroorganismen besiedelt und im Einzelfall auch verstoffwechselt werden können. Gerade an unzureichend belüfteten Stellen, so z. B. zwischen Schränken oder Möbeln und der tapezierten Wand, kann es so zu einer mikrobiellen Belastung, z. B. durch Schimmelpilze, kommen. Natural textiles in particular are able to remove water vapor from the room in their fibers absorb and release again and thus ensure a healthy, pleasant indoor climate. However, this water vapor absorption capacity also poses a risk of contamination because the fibers have large surfaces that are populated by microorganisms and in individual cases can also be metabolized. Especially in inadequately ventilated areas, e.g. B. between cabinets or furniture and the wallpapered wall, it can become a microbial Load, e.g. B. by mold.

Durch Einsatz von Aminoalkoholen im Verlauf des Herstellverfahrens der Textiltapeten lassen sich diese Einschränkungen problemlos beseitigen. Die Aminoalkohole können sich dabei sowohl in Papierträger als auch in den Fasern oder Fäden befinden. Leave by using amino alcohols in the course of the manufacturing process of the textile wallpaper remove these restrictions without any problems. The amino alcohols can both in paper backing and in the fibers or threads.

RauhfasertapetenWoodchip wallpaper

Bei Rauhfasertapeten werden Holzfasern und weitere Hilfsstoffe zur Herstellung verwendet. Dies geschieht dadurch, dass die angeteigten Holzfasern zwischen zwei Papierlagen eingebunden werden. Die Holzfasern nehmen, bedingt durch ihre große Oberfläche, grössere Mengen an Wasserdampf auf, was analog zu den Textiltapeten unter ungünstigen Raumbedingungen zu mikrobiellen Verkeimungen führen kann. Die Aminoalkohole können den Holzfasern oder dem Papierteig beigemischt werden. Woodchips and other auxiliaries are used in the production of woodchip wallpaper. This happens because the pasted wood fibers between two layers of paper be involved. Due to their large surface area, the wood fibers take larger ones Amounts of water vapor on what is analogous to the textile wallpaper under unfavorable Room conditions can lead to microbial contamination. The amino alcohols can be mixed with the wood fibers or the paper dough.

Zur weiteren Beschreibung der vorliegenden Erfindung werden die folgenden Beispiele gegeben, welche die Erfindung weiter erläutern, nicht aber ihren Umfang begrenzen sollen, wie er in den Patentansprüchen dargelegt ist. To further describe the present invention, the following examples given, which explain the invention further, but are not intended to limit its scope as described in the claims are set out.

example 1

In einen 400 mL Polypropylenbecher werden 27 g Dioctylphthalat, 13 g Bärostab KK 47 S (Mischmetallstabilisator der Firma Bärlocher), 28 g Azodicarbonamid, 50 g Titandioxid, 136 g Kalziumcarbonat, 5,2 g Wasser und 22 g Isoparaffin eingewogen. Anschließend wird die Mischung mit einem Spatel untergerührt und 4 Minuten mit einem Dissolver homogenisiert. Von dieser Mischung wird eine Probe von 21 g entnommen und zusammen mit 24 g Di-2- Ethylhexyl-phthalat, 5 g 2-tert.-Butylaminoethanol und 46 g Polyvinylchlorid in einen 400 mL Polypropylenbecher gegeben. Diese Mischung wird mit einem Spatel vorsichtig untergerührt und anschließend mit einem Dissolver 1 Minute lang homogenisiert, dann für 2 Stunden ruhen gelassen. 27 g of dioctyl phthalate and 13 g of KK 47 S bar are placed in a 400 mL polypropylene beaker (Mixed metal stabilizer from Bärlocher), 28 g azodicarbonamide, 50 g titanium dioxide, 136 g Calcium carbonate, 5.2 g water and 22 g isoparaffin weighed out. Then the Mix in with a spatula and homogenize for 4 minutes with a dissolver. A sample of 21 g is taken from this mixture and together with 24 g of Di-2- Ethylhexyl phthalate, 5 g of 2-tert-butylaminoethanol and 46 g of polyvinyl chloride in a 400 mL Given polypropylene cup. This mixture is carefully mixed in with a spatula and then homogenized with a dissolver for 1 minute, then rest for 2 hours calmly.

Example 1a

In einen Spannrahmen der Größe 30 mal 40 cm wird ein Tapetenpapier eingelegt. Der Spannrahmen wird in einen auf 200°C vorgeheizten Ofen für die Dauer von 15 Sekunden eingehängt, um eine Straffung des Papiers zu erreichen. Im Anschluß wird die Mischung aus Beispiel 1 auf eine Endseite des Papiers aufgebracht und mit einem 300 Mikrometer Rakel auf das Papier aufgetragen. Das so beschichtete Papier wird nun für die Dauer von 60 Sekunden in einen Ofen von 200°C eingebracht und aufgeschäumt, entnommen und auf Raumtemperatur abgekühlt. Aus diesem beschichteten Tapetenpapier wird eine Probe von 4 mal 3 cm ausgeschnitten. A wallpaper paper is inserted into a stenter frame size 30 by 40 cm. The The stenter is placed in an oven preheated to 200 ° C for 15 seconds mounted to tighten the paper. Then the mixture is made Example 1 applied to one end side of the paper and applied with a 300 micron doctor blade applied the paper. The paper coated in this way is now in for a period of 60 seconds an oven of 200 ° C was introduced and foamed, removed and brought to room temperature cooled. A sample of 4 by 3 cm is made from this coated wallpaper paper cut out.

Example 1b

Das beschichtete Tapetenstück aus Beispiel 1a wird auf den Boden eines Becherglases gelegt, das 10 mL einer Testkeimsuspension von Pseudomonas aeruginosa enthält. Das so vorbereitete System wird nun für die Dauer von 4 Stunden geschüttelt. Danach wird 1 mL der Testkeimsuspension entnommen. Nach Ablauf dieser Zeit ist die Keimzahl von 10⁷ auf 10³ Keime pro mL gesunken. The coated piece of wallpaper from Example 1a is placed on the bottom of a beaker containing 10 mL of a test germ suspension of Pseudomonas aeruginosa. The system prepared in this way is now shaken for a period of 4 hours. Then 1 mL of the test germ suspension is removed. After this time the number of germs decreased from 10 ⁷ to 10 ³ germs per mL.

Example 1c

Das beschichtete Tapetenstück aus Beispiel 1a wird auf den Boden eines Becherglases gelegt, das 10 mL einer Testkeimsuspension von Staphylococcus aureus enthält. Das so vorbereitete System wird nun für die Dauer von 4 Stunden geschüttelt. Danach wird 1 mL der Testkeimsuspension entnommen. Nach Ablauf dieser Zeit sind keine Keime von Staphylococcus aureus mehr nachweisbar. The coated piece of wallpaper from Example 1a is placed on the bottom of a beaker, containing 10 mL of a test germ suspension of Staphylococcus aureus. The so prepared System is now shaken for 4 hours. Then 1 mL of Test microbial suspension removed. After this time there are no germs from Staphylococcus aureus more detectable.

Example 1d

Je ein beschichtetes Tapetenstück aus Beispiel 1a wird mit Chlorella sp., Trentepohlia sp., Gloeocapsa sp. Calothrix sp. und Aspergilus niger beimpft. Diese Proben werden im Anschluß für 3 Wochen in einen Brutschrank verbracht. Im Gegensatz zu mitlaufenden Kontrollproben ist bei keinem der imprägnierten Proben ein Bewuchs feststellbar. A coated piece of wallpaper from example 1a is coated with Chlorella sp., Trentepohlia sp. Gloeocapsa sp. Calothrix sp. and Aspergilus niger. These samples will follow spent in an incubator for 3 weeks. In contrast to accompanying control samples no growth can be detected in any of the impregnated samples.

Example 2

In einen 400 mL Polypropylenbecher werden 27 g Dioctylphthalat, 13 g Bärostab KK 47 S (Mischmetallstabilisator der Firma Bärlocher), 28 g Azodicarbonamid, 50 g Titandioxid, 136 g Kalziumcarbonat, 5,2 g Wasser und 22 g Isoparaffin eingewogen. Anschließend wird die Mischung mit einem Spatel untergerührt und 4 Minuten mit einem Dissolver homogenisiert. Von dieser Mischung wird eine Probe von 21 g entnommen und zusammen mit 24 g Di-2- Ethylhexyl-phthalat, 3 g 3-Aminopropanol und 46 g Polyvinylchlorid in einen 400 mL Polypropylenbecher gegeben. Diese Mischung wird mit einem Spatel vorsichtig untergerührt und anschließend mit einem Dissolver 1 Minute lang homogenisiert, dann für 2 Stunden ruhen gelassen. 27 g of dioctyl phthalate and 13 g of KK 47 S bar are placed in a 400 mL polypropylene beaker (Mixed metal stabilizer from Bärlocher), 28 g azodicarbonamide, 50 g titanium dioxide, 136 g Calcium carbonate, 5.2 g water and 22 g isoparaffin weighed out. Then the Mix in with a spatula and homogenize for 4 minutes with a dissolver. A sample of 21 g is taken from this mixture and together with 24 g of Di-2- Ethylhexyl phthalate, 3 g of 3-aminopropanol and 46 g of polyvinyl chloride in a 400 mL Given polypropylene cup. This mixture is carefully mixed in with a spatula and then homogenized with a dissolver for 1 minute, then rest for 2 hours calmly.

Example 2a

In einen Spannrahmen der Größe 30 mal 40 cm wird ein Tapetenpapier eingelegt. Der Spannrahmen wird in einen auf 200°C vorgeheizten Ofen für die Dauer von 15 Sekunden eingehängt, um eine Straffung des Papiers zu erreichen. Im Anschluß wird die Mischung aus Beispiel 2 auf eine Endseite des Papiers aufgebracht und mit einem 300 Mikrometer Rakel auf das Papier aufgetragen. Das so beschichtete Papier wird nun für die Dauer von 60 Sekunden in einen Ofen von 200°C eingebracht und aufgeschäumt, entnommen und auf Raumtemperatur abgekühlt. Aus diesem beschichteten Tapetenpapier wird eine Probe von 4 mal 3 cm ausgeschnitten. A wallpaper paper is inserted into a stenter frame size 30 by 40 cm. The The stenter is placed in an oven preheated to 200 ° C for 15 seconds mounted to tighten the paper. Then the mixture is made Example 2 applied to one end of the paper and applied with a 300 micron doctor blade applied the paper. The paper coated in this way is now in for a period of 60 seconds an oven of 200 ° C was introduced and foamed, removed and brought to room temperature cooled. A sample of 4 by 3 cm is made from this coated wallpaper paper cut out.

Example 2b

Das beschichtete Tapetenstück aus Beispiel 2a wird auf den Boden eines Becherglases gelegt, das 10 mL einer Testkeimsuspension von Pseudomonas aeruginosa enthält. Das so vorbereitete System wird nun für die Dauer von 4 Stunden geschüttelt. Danach wird 1 mL der Testkeimsuspension entnommen. Nach Ablauf dieser Zeit ist die Keimzahl von 10⁷ auf 10²Keime pro mL gesunken. The coated piece of wallpaper from Example 2a is placed on the bottom of a beaker containing 10 mL of a test microbial suspension of Pseudomonas aeruginosa. The system prepared in this way is now shaken for a period of 4 hours. Then 1 mL of the test germ suspension is removed. After this time the number of germs decreased from 10 ⁷ to 10 ² germs per mL.

Example 2c

Das beschichtete Tapetenstück aus Beispiel 2a wird auf den Boden eines Becherglases gelegt, das 10 mL einer Testkeimsuspension von Staphylococcus aureus enthält. Das so vorbereitete System wird nun für die Dauer von 4 Stunden geschüttelt. Danach wird 1 mL der Testkeimsuspension entnommen. Nach Ablauf dieser Zeit sind keine Keime von Staphylococcus aureus mehr nachweisbar. The coated piece of wallpaper from example 2a is placed on the bottom of a beaker, containing 10 mL of a test germ suspension of Staphylococcus aureus. The so prepared System is now shaken for 4 hours. Then 1 mL of Test microbial suspension removed. After this time there are no germs from Staphylococcus aureus more detectable.

Example 2d

Je ein beschichtetes Tapetenstück aus Beispiel 2a wird mit Chlorella sp., Trentepohlia sp., Gloeocapsa sp. Calothrix sp. und Aspergilus niger beimpft. Diese Proben werden im Anschluß für 3 Wochen in einen Brutschrank verbracht. Im Gegensatz zu mitlaufenden Kontrollproben ist bei keinem der imprägnierten Proben ein Bewuchs feststellbar. Each coated piece of wallpaper from Example 2a is coated with Chlorella sp., Trentepohlia sp. Gloeocapsa sp. Calothrix sp. and Aspergilus niger. These samples will follow spent in an incubator for 3 weeks. In contrast to accompanying control samples no growth can be detected in any of the impregnated samples.

Example 3

In einen 400 mL Polypropylenbecher werden 27 g Dioctylphthalat, 13 g Bärostab KK 47 S (Mischmetallstabilisator der Firma Bärlocher), 28 g Azodicarbonamid, 50 g Titandioxid, 136 g Kalziumcarbonat, 5,2 g Wasser und 22 g Isoparaffin eingewogen. Anschließend wird die Mischung mit einem Spatel untergerührt und 4 Minuten mit einem Dissolver homogenisiert. Von dieser Mischung wird eine Probe von 21 g entnommen und zusammen mit 22 g Di-2- Ethylhexyl-phthalat, 1 g 3-Aminopropanol und 43 g Polyvinylchlorid in einen 400 mL Polypropylenbecher gegeben. Diese Mischung wird mit einem Spatel vorsichtig untergerührt und anschließend mit einem Dissolver 1 Minute lang homogenisiert, dann für 2 Stunden ruhen gelassen. 27 g of dioctyl phthalate and 13 g of KK 47 S bar are placed in a 400 mL polypropylene beaker (Mixed metal stabilizer from Bärlocher), 28 g azodicarbonamide, 50 g titanium dioxide, 136 g Calcium carbonate, 5.2 g water and 22 g isoparaffin weighed out. Then the Mix in with a spatula and homogenize for 4 minutes with a dissolver. A sample of 21 g is taken from this mixture and together with 22 g of Di-2- Ethylhexyl phthalate, 1 g of 3-aminopropanol and 43 g of polyvinyl chloride in a 400 mL Given polypropylene cup. This mixture is carefully mixed in with a spatula and then homogenized with a dissolver for 1 minute, then rest for 2 hours calmly.

Example 3a

In einen Spannrahmen der Größe 30 mal 40 cm wird ein Tapetenpapier eingelegt. Der Spannrahmen wird in einen auf 200°C vorgeheizten Ofen für die Dauer von 15 Sekunden eingehängt, um eine Straffung des Papiers zu erreichen. Im Anschluß wird die Mischung aus Beispiel 3 auf eine Endseite des Papiers aufgebracht und mit einem 300 Mikrometer Rakel auf das Papier aufgetragen. Das so beschichtete Papier wird nun für die Dauer von 60 Sekunden in einen Ofen von 200°C eingebracht und aufgeschäumt, entnommen und auf Raumtemperatur abgekühlt. Aus diesem beschichteten Tapetenpapier wird eine Probe von 4 mal 3 cm ausgeschnitten. A wallpaper paper is inserted into a stenter frame size 30 by 40 cm. The The stenter is placed in an oven preheated to 200 ° C for 15 seconds mounted to tighten the paper. Then the mixture is made Example 3 applied to one end side of the paper and applied with a 300 micron doctor blade applied the paper. The paper coated in this way is now in for a period of 60 seconds an oven of 200 ° C was introduced and foamed, removed and brought to room temperature cooled. A sample of 4 by 3 cm is made from this coated wallpaper paper cut out.

Example 3b

Das beschichtete Tapetenstück aus Beispiel 3a wird auf den Boden eines Becherglases gelegt, das 10 mL einer Testkeimsuspension von Pseudomonas aeruginosa enthält. Das so vorbereitete System wird nun für die Dauer von 4 Stunden geschüttelt. Danach wird 1 mL der Testkeimsuspension entnommen. Nach Ablauf dieser Zeit ist die Keimzahl von 10⁷ auf 10⁴ Keime pro mL gesunken. The coated piece of wallpaper from example 3a is placed on the bottom of a beaker containing 10 ml of a test germ suspension of Pseudomonas aeruginosa. The system prepared in this way is now shaken for a period of 4 hours. Then 1 mL of the test germ suspension is removed. After this time the number of germs decreased from 10 ⁷ to 10 ⁴ germs per mL.

Example 3c

Das beschichtete Tapetenstück aus Beispiel 3a wird auf den Boden eines Becherglases gelegt, das 10 mL einer Testkeimsuspension von Staphylococcus aureus enthält. Das so vorbereitete System wird nun für die Dauer von 4 Stunden geschüttelt. Danach wird 1 mL der Testkeimsuspension entnommen. Nach Ablauf dieser Zeit ist die Keimzahl von 10⁷ auf 10³ Keime pro mL gesunken. The coated piece of wallpaper from Example 3a is placed on the bottom of a beaker containing 10 mL of a test germ suspension of Staphylococcus aureus. The system prepared in this way is now shaken for a period of 4 hours. Then 1 mL of the test germ suspension is removed. After this time the number of germs decreased from 10 ⁷ to 10 ³ germs per mL.

Example 3d

Je ein beschichtetes Tapetenstück aus Beispiel 3a wird mit Chlorella sp., Trentepohlia sp., Gloeocapsa sp. Calothrix sp. und Aspergilus niger beimpft. Diese Proben werden im Anschluß für 3 Wochen in einen Brutschrank verbracht. Im Gegensatz zu mitlaufenden Kontrollproben ist bei keinem der imprägnierten Proben ein Bewuchs feststellbar. Each coated piece of wallpaper from Example 3a is coated with Chlorella sp., Trentepohlia sp. Gloeocapsa sp. Calothrix sp. and Aspergilus niger. These samples will follow spent in an incubator for 3 weeks. In contrast to accompanying control samples no growth can be detected in any of the impregnated samples.

Example 4

In einen 400 mL Polypropylenbecher werden 27 g Dioctylphthalat, 13 g Bärostab KK 47 S (Mischmetallstabilisator der Firma Bärlocher), 28 g Azodicarbonamid, 50 g Titandioxid, 136 g Kalziumcarbonat, 5,2 g Wasser und 22 g Isoparaffin eingewogen. Anschließend wird die Mischung mit einem Spatel untergerührt und 4 Minuten mit einem Dissolver homogenisiert. Von dieser Mischung wird eine Probe von 21 g entnommen und zusammen mit 27 g Di-2- Ethylhexyl-phthalat, 10 g 2-Butylaminoethanol und 50 g Polyvinylchlorid in einen 400 mL Polypropylenbecher gegeben. Diese Mischung wird mit einem Spatel vorsichtig untergerührt und anschließend mit einem Dissolver 1 Minute lang homogenisiert, dann für 2 Stunden ruhen gelassen. 27 g of dioctyl phthalate and 13 g of KK 47 S bar are placed in a 400 mL polypropylene beaker (Mixed metal stabilizer from Bärlocher), 28 g azodicarbonamide, 50 g titanium dioxide, 136 g Calcium carbonate, 5.2 g water and 22 g isoparaffin weighed out. Then the Mix in with a spatula and homogenize for 4 minutes with a dissolver. A sample of 21 g is taken from this mixture and together with 27 g of Di-2- Ethylhexyl phthalate, 10 g 2-butylaminoethanol and 50 g polyvinyl chloride in a 400 mL Given polypropylene cup. This mixture is carefully mixed in with a spatula and then homogenized with a dissolver for 1 minute, then rest for 2 hours calmly.

Example 4a

In einen Spannrahmen der Größe 30 mal 40 cm wird ein Tapetenpapier eingelegt. Der Spannrahmen wird in einen auf 200°C vorgeheizten Ofen für die Dauer von 15 Sekunden eingehängt, um eine Straffung des Papiers zu erreichen. Im Anschluß wird die Mischung aus Beispiel 4 auf eine Endseite des Papiers aufgebracht und mit einem 300 Mikrometer Rakel auf das Papier aufgetragen. Das so beschichtete Papier wird nun für die Dauer von 60 Sekunden in einen Ofen von 200°C eingebracht und aufgeschäumt, entnommen und auf Raumtemperatur abgekühlt. Aus diesem beschichteten Tapetenpapier wird eine Probe von 4 mal 3 cm ausgeschnitten. A wallpaper paper is inserted into a stenter frame size 30 by 40 cm. The The stenter is placed in an oven preheated to 200 ° C for 15 seconds mounted to tighten the paper. Then the mixture is made Example 4 applied to one end side of the paper and applied with a 300 micron doctor blade applied the paper. The paper coated in this way is now in for a period of 60 seconds an oven of 200 ° C was introduced and foamed, removed and brought to room temperature cooled. A sample of 4 by 3 cm is made from this coated wallpaper paper cut out.

Example 4b

Das beschichtete Tapetenstück aus Beispiel 4a wird auf den Boden eines Becherglases gelegt, das 10 mL einer Testkeimsuspension von Pseudomonas aeruginosa enthält. Das so vorbereitete System wird nun für die Dauer von 4 Stunden geschüttelt. Danach wird 1 mL der Testkeimsuspension entnommen. Nach Ablauf dieser Zeit ist die Keimzahl von 10⁷ auf 10⁴ Keime pro mL gesunken. The coated piece of wallpaper from example 4a is placed on the bottom of a beaker containing 10 ml of a test germ suspension of Pseudomonas aeruginosa. The system prepared in this way is now shaken for a period of 4 hours. Then 1 mL of the test germ suspension is removed. After this time the number of germs decreased from 10 ⁷ to 10 ⁴ germs per mL.

Example 4c

Das beschichtete Tapetenstück aus Beispiel 4a wird auf den Boden eines Becherglases gelegt, das 10 mL einer Testkeimsuspension von Staphylococcus aureus enthält. Das so vorbereitete System wird nun für die Dauer von 4 Stunden geschüttelt. Danach wird 1 mL der Testkeimsuspension entnommen. Nach Ablauf dieser Zeit sind keine Keime von Staphylococcus aureus mehr nachweisbar. The coated piece of wallpaper from Example 4a is placed on the bottom of a beaker, containing 10 mL of a test germ suspension of Staphylococcus aureus. The so prepared System is now shaken for 4 hours. Then 1 mL of Test microbial suspension removed. After this time there are no germs from Staphylococcus aureus more detectable.

Example 4d

Je ein beschichtetes Tapetenstück aus Beispiel 4a wird mit Chlorella sp., Trentepohlia sp., Gloeocapsa sp. Calothrix sp. und Aspergilus niger beimpft. Diese Proben werden im Anschluß für 3 Wochen in einen Brutschrank verbracht. Im Gegensatz zu mitlaufenden Kontrollproben ist bei keinem der imprägnierten Proben ein Bewuchs feststellbar. Each coated piece of wallpaper from Example 4a is coated with Chlorella sp., Trentepohlia sp. Gloeocapsa sp. Calothrix sp. and Aspergilus niger. These samples will follow spent in an incubator for 3 weeks. In contrast to accompanying control samples no growth can be detected in any of the impregnated samples.

Example 5

In einen 400 mL Polypropylenbecher werden 27 g Dioctylphthalat, 13 g Bärostab KK 47 S (Mischmetallstabilisator der Firma Bärlocher), 28 g Azodicarbonamid, 50 g Titandioxid, 136 g Kalziumcarbonat, 5,2 g Wasser und 22 g Isoparaffin eingewogen. Anschließend wird die Mischung mit einem Spatel untergerührt und 4 Minuten mit einem Dissolver homogenisiert. Von dieser Mischung wird eine Probe von 21 g entnommen und zusammen mit 28 g Di-2- Ethylhexyl-phthalat, 8 g 2-tert.-Butylaminoethanol und 53 g Polyvinylchlorid in einen 400 mL Polypropylenbecher gegeben. Diese Mischung wird mit einem Spatel vorsichtig untergerührt und anschließend mit einem Dissolver 1 Minute lang homogenisiert, dann für 2 Stunden ruhen gelassen. 27 g of dioctyl phthalate and 13 g of KK 47 S bar are placed in a 400 mL polypropylene beaker (Mixed metal stabilizer from Bärlocher), 28 g azodicarbonamide, 50 g titanium dioxide, 136 g Calcium carbonate, 5.2 g water and 22 g isoparaffin weighed out. Then the Mix in with a spatula and homogenize for 4 minutes with a dissolver. A sample of 21 g is taken from this mixture and together with 28 g of Di-2- Ethylhexyl phthalate, 8 g of 2-tert-butylaminoethanol and 53 g of polyvinyl chloride in a 400 mL Given polypropylene cup. This mixture is carefully mixed in with a spatula and then homogenized with a dissolver for 1 minute, then rest for 2 hours calmly.

Example 5a

In einen Spannrahmen der Größe 30 mal 40 cm wird ein Tapetenpapier eingelegt. Der Spannrahmen wird in einen auf 200°C vorgeheizten Ofen für die Dauer von 15 Sekunden eingehängt, um eine Straffung des Papiers zu erreichen. Im Anschluß wird die Mischung aus Beispiel 5 auf eine Endseite des Papiers aufgebracht und mit einem 300 Mikrometer Rakel auf das Papier aufgetragen. Das so beschichtete Papier wird nun für die Dauer von 60 Sekunden in einen Ofen von 200°C eingebracht und aufgeschäumt, entnommen und auf Raumtemperatur abgekühlt. Aus diesem beschichteten Tapetenpapier wird eine Probe von 4 mal 3 cm ausgeschnitten. A wallpaper paper is inserted into a stenter frame size 30 by 40 cm. The The stenter is placed in an oven preheated to 200 ° C for 15 seconds mounted to tighten the paper. Then the mixture is made Example 5 applied to one end side of the paper and applied with a 300 micron doctor blade applied the paper. The paper coated in this way is now in for a period of 60 seconds an oven of 200 ° C was introduced and foamed, removed and brought to room temperature cooled. A sample of 4 by 3 cm is made from this coated wallpaper paper cut out.

Example 5b

Das beschichtete Tapetenstück aus Beispiel 5a wird auf den Boden eines Becherglases gelegt, das 10 mL einer Testkeimsuspension von Pseudomonas aeruginosa enthält. Das so vorbereitete System wird nun für die Dauer von 4 Stunden geschüttelt. Danach wird 1 mL der Testkeimsuspension entnommen. Nach Ablauf dieser Zeit sind keine Keime von Pseudomonas aeruginosa mehr nachweisbar. The coated piece of wallpaper from Example 5a is placed on the bottom of a beaker, containing 10 mL of a test microbial suspension of Pseudomonas aeruginosa. The so prepared System is now shaken for 4 hours. Then 1 mL of Test microbial suspension removed. After this time, there are no Pseudomonas germs aeruginosa more detectable.

Example 5c

Das beschichtete Tapetenstück aus Beispiel 5a wird auf den Boden eines Becherglases gelegt, das 10 mL einer Testkeimsuspension von Staphylococcus aureus enthält. Das so vorbereitete System wird nun für die Dauer von 4 Stunden geschüttelt. Danach wird 1 mL der Testkeimsuspension entnommen. Nach Ablauf dieser Zeit sind keine Keime von Staphylococcus aureus mehr nachweisbar. The coated piece of wallpaper from Example 5a is placed on the bottom of a beaker, containing 10 mL of a test germ suspension of Staphylococcus aureus. The so prepared System is now shaken for 4 hours. Then 1 mL of Test microbial suspension removed. After this time there are no germs from Staphylococcus aureus more detectable.

Example 5d

Je ein beschichtetes Tapetenstück aus Beispiel 5a wird mit Chlorella sp., Trentepohlia sp., Gloeocapsa sp. Calothrix sp. und Aspergilus niger beimpft. Diese Proben werden im Anschluß für 3 Wochen in einen Brutschrank verbracht. Im Gegensatz zu mitlaufenden Kontrollproben ist bei keinem der imprägnierten Proben ein Bewuchs feststellbar. Each coated piece of wallpaper from Example 5a is coated with Chlorella sp., Trentepohlia sp. Gloeocapsa sp. Calothrix sp. and Aspergilus niger. These samples will follow spent in an incubator for 3 weeks. In contrast to accompanying control samples no growth can be detected in any of the impregnated samples.

Claims

1. Wallpaper containing 0.01-40 wt .-% of at least one amino alcohol.

2. Wallpaper according to claim 1, characterized, that the wallpaper is a mixture of vinyl polymers and at least one amino alcohol contains.

3. Wallpaper according to claim 1, characterized, that the wallpaper is a mixture of paper fibers and / or cellulose and / or textile fibers with at least one amino alcohol.

4. Wallpaper according to claim 1, characterized, that the wallpaper is made of a paper backing with a coating that has at least one Contains amino alcohol.

5. Wallpaper according to claim 4, characterized, that the coating is PVC, polyurethane, polymethyl methacrylate, polyethylene, Contains polypropylene and / or their blends and at least one amino alcohol.

6. Wallpaper according to one of claims 1 to 5, characterized in that an amino alcohol of the formula I
With

R1 = branched or unbranched aliphatic or aromatic hydrocarbon radical with 1 to 15 carbon atoms.
R2 = H, branched or unbranched aliphatic or aromatic hydrocarbon radical with 1 to 15 carbon atoms.
R3 = H, branched or unbranched aliphatic or aromatic hydrocarbon radical with 1 to 15 carbon atoms.
is used.

7. Wallpaper according to one of claims 1 to 6, characterized, that one or more amino alcohols from the group tert.-butylaminoethanol, tert.- Butylaminomethanol, tert-butylaminopropanol, 2-butylaminoethanol, 2- Butylaminomethanol, 2-butylaminopropanol, 2-diethylaminoethanol, 2-diethylaminomethanol, 2-diethylaminopropanol, 2-dimethylaminoethanol, 2-dimethylaminomethanol, 2-dimethylaminopropanol, aminomethanol, aminoethanol, aminopropanol or Aminobutanol can be used.

8. Process for the production of antimicrobial wallpapers, characterized, that a paper support with a coating containing at least one amino alcohol is provided.

9. The method according to claim 8, characterized, that the coating is a polymer or a polymer blend.

10. The method according to claim 8 or 9, characterized, that the coating by thermal gelation of a plastisol containing 0.01-40 % By weight of at least one amino alcohol is produced.

11. Process for the production of antimicrobial wallpapers, characterized, the textile, cotton, jute, silk, viscose or polymer fibers, the 0.01-40 wt. % contain at least one amino alcohol, attached to a paper support.

12. Process for the production of antimicrobial wallpapers, characterized, the textile, cotton, jute, silk, viscose or polymer fibers in one Paper carrier, containing 0.01-40 wt .-% of at least one amino alcohol attached become.

13. Process for the production of antimicrobial wallpapers, characterized, that a mixture of paper and / or cellulose and / or textiles and / or cellulose and / or wood particles and / or woodchips 0.01-40% by weight of at least one Amino alcohol is added and this mixture is processed into a paper support becomes.

14. The method according to any one of claims 8 to 13, characterized in that an amino alcohol of formula I.
With

R1 = branched or unbranched aliphatic or aromatic hydrocarbon radical with 1 to 15 carbon atoms.
R2 = H, branched or unbranched aliphatic or aromatic hydrocarbon radical with 1 to 15 carbon atoms.
R3 = H, branched or unbranched aliphatic or aromatic hydrocarbon radical with 1 to 15 carbon atoms.
is used.

15. The method according to any one of claims 8 to 14, characterized, that one or more amino alcohols from the group tert.-butylaminoethanol, tert.- Butylaminomethanol, tert-butylaminopropanol, 2-butylaminoethanol, 2- Butylaminomethanol, 2-butylaminopropanol, 2-diethylaminoethanol, 2-diethylaminomethanol, 2-diethylaminopropanol, 2-dimethylaminoethanol, 2-dimethylaminomethanol, 2-dimethylaminopropanol, aminomethanol, aminoethanol, aminopropanol or Aminobutanol can be used.