WO1999022880A1 - Substrate treatment promoting shedding of oil - Google Patents
Substrate treatment promoting shedding of oil Download PDFInfo
- Publication number
- WO1999022880A1 WO1999022880A1 PCT/US1998/017764 US9817764W WO9922880A1 WO 1999022880 A1 WO1999022880 A1 WO 1999022880A1 US 9817764 W US9817764 W US 9817764W WO 9922880 A1 WO9922880 A1 WO 9922880A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- sensing device
- oil level
- level sensing
- treating
- oil
- Prior art date
Abstract
Description
Claims