WO2009009641A2 - Coating for decorative metals with improved mar and scratch resistance and methods of application - Google Patents
Coating for decorative metals with improved mar and scratch resistance and methods of application Download PDFInfo
- Publication number
- WO2009009641A2 WO2009009641A2 PCT/US2008/069602 US2008069602W WO2009009641A2 WO 2009009641 A2 WO2009009641 A2 WO 2009009641A2 US 2008069602 W US2008069602 W US 2008069602W WO 2009009641 A2 WO2009009641 A2 WO 2009009641A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- groups
- coated article
- coating
- inorganic particles
- Prior art date
Abstract
Description
Claims