WO2013014546A2 - Superhydrophobic surfaces - Google Patents
Superhydrophobic surfaces Download PDFInfo
- Publication number
- WO2013014546A2 WO2013014546A2 PCT/IB2012/053062 IB2012053062W WO2013014546A2 WO 2013014546 A2 WO2013014546 A2 WO 2013014546A2 IB 2012053062 W IB2012053062 W IB 2012053062W WO 2013014546 A2 WO2013014546 A2 WO 2013014546A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- water
- superhydrophobic surface
- fibers
- substrate
- hydrophobic
- Prior art date
Abstract
Description
Claims